描述
Zytel 70G30L NC010 PA66 is a 30% glass fiber reinforced polyamide 66 resin designed for injection molding applications. It provides higher stiffness, strength and dimensional stability than unreinforced PA66 while maintaining good toughness, chemical resistance and processing performance.
This grade is identified as PA66-GF30 and is commonly used in automotive, furniture, domestic appliance, sporting goods and construction applications. Public technical data lists density around 1.37 g/cm³, tensile modulus around 9800–10000 MPa, tensile strength around 195 MPa and melting temperature around 262°C.
Zytel 70G30L NC010 PA66 Key Features
- 30% glass fiber reinforced PA66
- Natural color NC010
- High stiffness and strength
- Good dimensional stability
- Low molding shrinkage
- Lubricated for stable processing
- Good heat resistance
- Suitable for injection molding
Zytel 70G30L NC010 PA66 Typical Applications
- Automotive components
- Electrical connectors
- Appliance parts
- Furniture hardware
- Sporting goods
- Construction parts
- Industrial mechanical parts
- Reinforced engineering components
Related Products
Zytel 70G30L NC010 PA66 Typical Properties
| Property | Typical Value |
|---|---|
| Material | PA66-GF30 |
| Grade | 70G30L NC010 |
| Color | Natural |
| Glass Fiber Content | 30% |
| Density | 1.37 g/cm³ |
| Tensile Modulus | 9800–10000 MPa |
| Tensile Strength | 195 MPa |
| Charpy Notched Impact, 23°C | 13 kJ/m² |
| HDT, 1.8 MPa | 253°C |
| Melting Temperature | 262°C |
| Processing Method | Injection Molding |
Advantages
Zytel 70G30L NC010 PA66 is suitable for applications requiring high rigidity, mechanical strength and dimensional stability. The 30% glass fiber reinforcement improves stiffness and reduces shrinkage compared with unfilled PA66.
This grade is useful for automotive, electrical and industrial molded parts where stable injection molding, good strength and reliable long-term performance are required.
Processing Recommendations
Zytel 70G30L NC010 PA66 is recommended for injection molding. Drying before processing is required to reduce moisture and maintain good surface quality, dimensional stability and mechanical performance. Processing conditions should be adjusted according to part thickness, mold design and glass fiber orientation.
For official product information, please refer to the Celanese Zytel PA official product page .
For technical reference, please refer to the Zytel 70G30L NC010 technical datasheet .