Zytel 70G30HSL BK039B PA66 is a 30% glass fiber reinforced, heat stabilized polyamide 66 resin designed for injection molding applications. It provides significantly higher stiffness and strength than unreinforced PA66 while maintaining good dimensional stability, heat resistance and chemical resistance. Public datasheet information identifies this grade as PA66-GF30 for injection molding.
This black glass-filled nylon 66 grade is suitable for demanding molded components in automotive, furniture, domestic appliances, sporting goods and construction applications. Representative data lists tensile modulus around 10000 MPa, stress at break around 190 MPa, flexural modulus around 9000 MPa, molding shrinkage parallel around 0.3%, and transverse shrinkage around 1.1%.
Shenzhen Ruiqing International Trade Co., Ltd. supplies original Zytel 70G30HSL BK039B PA66 resin with quotation support, document assistance and global delivery service.
Zytel 70G30HSL BK039B PA66 Key Features
- 30% glass fiber reinforced PA66
- Heat stabilized formulation
- Black resin pellet form
- High stiffness and strength
- Excellent dimensional stability
- Low molding shrinkage
- Good heat resistance
- Suitable for injection molding
Zytel 70G30HSL BK039B PA66 Typical Applications
- Automotive injection molded parts
- Electrical and electronic components
- Appliance components
- Furniture hardware
- Sporting goods
- Construction components
- Industrial mechanical parts
- Reinforced engineering components
Advantages
Zytel 70G30HSL BK039B PA66 is suitable for applications requiring higher stiffness, strength and dimensional stability than lower glass-filled or unreinforced PA66 grades. The 30% glass fiber reinforcement improves rigidity and reduces shrinkage, making it useful for precision engineering components.
The heat stabilized formulation helps molded parts maintain performance during long-term exposure to elevated temperatures, making this grade practical for automotive, electrical and industrial applications.
Related Products
Zytel 70G30HSL BK039B PA66 Typical Properties
| Property | Typical Value |
|---|---|
| Material | PA66-GF30 |
| Grade | 70G30HSL BK039B |
| Color | Black |
| Glass Fiber Content | 30% |
| Density | 1.37 g/cm³ |
| Tensile Modulus | 10000 MPa |
| Stress at Break | 190 MPa |
| Flexural Modulus | 9000 MPa |
| Charpy Notched Impact, 23°C | 10 kJ/m² |
| Molding Shrinkage, Flow | 0.3% |
| Molding Shrinkage, Transverse | 1.1% |
| Processing Method | Injection Molding |
Processing Recommendations
Zytel 70G30HSL BK039B PA66 is recommended for injection molding. Drying before processing is required to reduce moisture and maintain surface quality, dimensional stability and mechanical performance. Public datasheet guidance lists drying temperature at ≥80°C, drying time 2–4 hours, processing moisture content ≤0.2%, and optimum melt temperature around 295°C.
For official product information, please refer to the Celanese Zytel PA official product page .
For technical reference, please refer to the Zytel 70G30HSL BK039B technical datasheet .
Zytel 70G30HSL BK039B PA66 FAQ
What is Zytel 70G30HSL BK039B PA66?
It is a 30% glass fiber reinforced, heat stabilized black PA66 resin designed for injection molding.
What does PA66-GF30 mean?
PA66-GF30 means polyamide 66 reinforced with approximately 30% glass fiber.
What is the main advantage of this grade?
It provides high stiffness, high strength, low shrinkage and good dimensional stability compared with unreinforced PA66.
Is Zytel 70G30HSL BK039B suitable for automotive applications?
Yes. It is suitable for automotive, electrical, appliance and industrial engineering components.
Can original Zytel 70G30HSL BK039B PA66 be supplied?
Yes. Shenzhen Ruiqing International Trade Co., Ltd. can supply original Zytel PA66 materials with quotation and document support.