Zytel 101L BKB080 PA66 is a lubricated polyamide 66 resin developed for injection molding applications. It combines high mechanical strength, stiffness, toughness and excellent wear resistance with improved mold release and processing stability, making it suitable for high-volume production of engineering components.
Following Celanese’s acquisition of DuPont’s Mobility & Materials business, Zytel® continues as one of the world’s best-known engineering nylon brands. Public product information describes Zytel 101L BKB080 as a lubricated PA66 injection molding grade with a density of approximately 1.14 g/cm³, tensile strength of 82 MPa, tensile modulus of 3100 MPa, HDT (0.45 MPa) of 200°C, and black pellet form.
Zytel 101L BKB080 PA66 offers good chemical resistance, abrasion resistance and dimensional stability. It is widely used in automotive components, electrical products, consumer appliances and industrial mechanical parts where long service life and reliable performance are required.
Shenzhen Ruiqing International Trade Co., Ltd. supplies original Zytel 101L BKB080 PA66 resin with technical support, stable sourcing and worldwide delivery.
Zytel 101L BKB080 PA66 Key Features
- Lubricated PA66 injection molding grade
- Black engineering resin
- High mechanical strength
- Excellent stiffness and toughness
- Good abrasion resistance
- Good chemical resistance
- Excellent heat resistance
- Stable processing performance
Zytel 101L BKB080 PA66 Typical Applications
- Automotive components
- Electrical connectors
- Household appliances
- Industrial machinery parts
- Furniture hardware
- Sporting goods
- Mechanical engineering parts
- Injection molded components
Advantages
Zytel 101L BKB080 PA66 is designed for manufacturers requiring a lubricated engineering nylon with stable molding performance and reliable mechanical properties.
Compared with standard unlubricated PA66 grades, its lubricated formulation improves mold release and processing efficiency while maintaining the high strength, stiffness and heat resistance expected from nylon 66.
Related Products
Zytel 101L BKB080 PA66 Typical Properties
| Property | Typical Value |
|---|---|
| Material | PA66 |
| Density | 1.14 g/cm³ |
| Tensile Strength | 82 MPa |
| Tensile Modulus | 3100 MPa |
| Notched Charpy Impact | 5.5 kJ/m² |
| HDT (0.45 MPa) | 200°C |
| HDT (1.82 MPa) | 70°C |
| Color | Black |
| Processing Method | Injection Molding |
Typical published information lists Zytel 101L BKB080 as a lubricated PA66 grade with the above representative physical and mechanical properties.
Processing Recommendations
Zytel 101L BKB080 PA66 is designed for injection molding. Drying before processing is recommended to reduce moisture content and achieve optimum mechanical properties, dimensional stability and surface appearance. Typical drying conditions are 80°C for 2–4 hours, with melt temperatures around 280–295°C, depending on part geometry and molding conditions.
For official product information, please refer to the Celanese Zytel® PA Official Product Page .
Zytel 101L BKB080 PA66 FAQ
What is Zytel 101L BKB080 PA66?
It is a lubricated black PA66 resin designed for injection molding applications.
What are the main advantages of Zytel 101L BKB080?
It provides high strength, good stiffness, excellent wear resistance, heat resistance and improved processing efficiency.
What industries commonly use this grade?
It is widely used in automotive, electrical, appliance, industrial machinery and consumer engineering products.
Is Zytel 101L BKB080 suitable for injection molding?
Yes. It is specifically developed as a lubricated PA66 injection molding grade.
Can original Zytel 101L BKB080 PA66 be supplied?
Yes. Shenzhen Ruiqing International Trade Co., Ltd. supplies original Celanese Zytel PA66 materials with technical documentation, quotation support and global shipping.