ULTEM Resin ATX200R is a high flow, unreinforced polyetherimide (PEI) blend manufactured by SABIC. As an authorized distributor and trader, we supply genuine SABIC materials with full traceability.
ULTEM ATX200R is a high flow PEI blend featuring internal mold release for improved demolding efficiency. It is specifically engineered for applications requiring a unique combination of high impact resistance, flame retardancy, and excellent processability. Key attributes include:
-
Internal Mold Release – Formulated with internal mold release agents for improved demolding and processing efficiency
-
High Flow – Exceptional flow characteristics (MVR 16 cm³/10min at 340°C/5kg) enable processing of complex, thin-walled parts
-
High Impact Resistance – Excellent toughness with notched Izod impact of 53 J/m and unnotched impact of 2,080 J/m
-
Flame Retardant – UL94 V-0 rated; non-halogenated flame retardant
-
High Heat Resistance – Vicat softening temperature of 210°C; UL RTI of 115°C
-
PFAS-Free – No PFAS intentionally added during manufacturing
-
High Stiffness & Strength – Flexural modulus of 3,100-3,170 MPa; tensile yield strength of 95-96 MPa
-
Excellent Dimensional Stability – Low shrinkage (0.50-0.70%) and low creep sensitivity
-
Low Smoke & Toxicity – Inherently low smoke and toxicity evolution
-
ECO Conforming – Meets environmental compliance standards
-
Versatile Processing – Suitable for injection molding
Key Features of ULTEM ATX200R
-
Internal Mold Release – Formulated with internal mold release agents for improved demolding and processing efficiency, reducing cycle times and improving part quality
-
High Flow PEI Blend – Exceptional flow characteristics (MVR 16 cm³/10min at 340°C/5kg; MFR 26.5 g/10min at 337°C/6.6kg) for processing complex, thin-walled parts
-
High Impact Resistance – Excellent toughness with notched Izod impact of 53 J/m; unnotched impact of 2,080 J/m; Charpy notched impact of 4 kJ/m²
-
Flame Retardant – UL94 V-0 rated; non-halogenated flame retardant; ECO Conforming
-
High Heat Resistance – Vicat softening temperature of 210°C (ISO A50); UL RTI of 115°C (Elec/Imp/Str)
-
High Mechanical Strength – Tensile modulus of 3,000-3,300 MPa; tensile yield strength of 95-96 MPa; flexural modulus of 3,100-3,170 MPa
-
Excellent Dimensional Stability – Low shrinkage (0.50-0.70%); low creep sensitivity; amorphous structure for predictable dimensional stability
-
Good Chemical Resistance – Excellent resistance to many chemicals and provides hydrolytic stability
-
Low Smoke & Low Toxicity – Inherently low smoke and toxicity evolution
-
Good Metal Adhesion – Suitable for applications requiring metal bonding
-
PFAS-Free – No PFAS intentionally added during manufacturing
-
ECO Conforming & RoHS Compliant – Meets environmental compliance standards
-
Versatile Processing – Suitable for injection molding
Typical Applications for ULTEM ATX200R
| Industry | Typical Applications |
|---|---|
| Automotive | Heavy truck, automotive under the hood, motorcycle, recreational/specialty vehicles |
| Aerospace | Aerospace applications |
| Electrical & Electronics | Electrical components, connectors, circuit boards, mobile phones, computers, tablets, lighting, speakers, earphones, wireless communication |
| Consumer Goods | Home appliances, commercial appliances, personal accessories, sport/leisure, furniture |
| Drone | Drone solutions |
| Healthcare & Medical | Surgical devices, pharmaceutical packaging & drug delivery, general healthcare, patient testing |
| Industrial | Material handling, textile, eyewear, industrial packaging |
| Mass Transportation | Rail applications |
| Building & Construction | Building components, water management |
| Personal & Professional Hygiene | Hygiene products |
ATX200 Series Comparison
| Property | ATX200 | ATX200F | ATX200R |
|---|---|---|---|
| Key Feature | High flow, high impact | High flow, high impact, FDA food contact | High flow, high impact, internal mold release |
| Internal Mold Release | No | No | Yes |
| US FDA Food Contact | No | Yes | No |
| UL 94 | V-0 / V-2 | V-0 / V-2 | V-0 |
| PFAS-Free | Yes | Yes | Yes |
| ECO Conforming | Yes | Yes | Yes |
Typical Properties
| Property | ULTEM ATX200R (ASTM) | ULTEM ATX200R (ISO) | Unit | Test Method |
|---|---|---|---|---|
| Physical | ||||
| Density / Specific Gravity | 1.26 | 1.26 | g/cm³ | ASTM D792 / ISO 1183 |
| Melt Flow Rate (MFR) – 337°C/6.6kg | 26.5 | — | g/10min | ASTM D1238 |
| Melt Volume Rate (MVR) – 340°C/5kg | — | 16 | cm³/10min | ISO 1133 |
| Mold Shrinkage, Flow (3.2mm) | 0.50 – 0.70 | — | % | SABIC Method |
| Mechanical | ||||
| Tensile Modulus — ASTM | 3,300 | — | MPa | ASTM D638 |
| Tensile Modulus — ISO | — | 3,000 | MPa | ISO 527 |
| Tensile Strength (Yield) — ASTM | 96 | — | MPa | ASTM D638 |
| Tensile Strength (Yield) — ISO | — | 95 | MPa | ISO 527 |
| Tensile Strength (Break) — ASTM | 85 | — | MPa | ASTM D638 |
| Tensile Strength (Break) — ISO | — | 75 | MPa | ISO 527 |
| Elongation at Yield | 7.0 | 6.5 | % | ASTM D638 / ISO 527 |
| Elongation at Break — ASTM | 70 | — | % | ASTM D638 |
| Strain at Break — ISO | — | 20 | % | ISO 527 |
| Flexural Modulus — ASTM | 3,170 | — | MPa | ASTM D790 |
| Flexural Modulus — ISO | — | 3,100 | MPa | ISO 178 |
| Izod Impact (Notched, 23°C) — ASTM | 53 | — | J/m | ASTM D256 |
| Izod Impact (Notched, 23°C) — ISO | — | 5 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 23°C) — ASTM | 2,080 | — | J/m | ASTM D256 |
| Charpy Impact (Notched, 23°C) — ISO | — | 4 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness — ISO | — | 125 | MPa | ISO 2039-1 |
| Thermal | ||||
| Glass Transition Temperature (Tg) | ~210 | ~210 | °C | |
| Heat Deflection Temp. (1.82MPa) — ASTM | ~191 | — | °C | ASTM D648 |
| Heat Deflection Temp. (1.8MPa) — ISO | — | ~180 | °C | ISO 75 |
| Vicat Softening Temp. (A50) — ISO | — | 210 | °C | ISO 306 |
| Vicat Softening Temp. (B50) | 210 | — | °C | ASTM D1525 |
| UL RTI (Elec/Imp/Str) | 115 | 115 | °C | UL 746B |
| Flammability | ||||
| UL 94 Flammability | V-0 | — | — | UL 94 |
Important Notes on Typical Data:
-
Values listed are typical and sourced from SABIC official data sheets. They do not constitute binding product specification.
-
Batch-to-batch deviations may exist. For critical applications, validate performance with batch-specific COA certificate.
-
Final performance depends on processing conditions, mold design, and part geometry.
-
SABIC official TDS shall serve as definitive technical reference. Request the latest official TDS from our sales team.
Processing Guidelines (Injection Molding)
| Parameter | Recommended Conditions | |
|---|---|---|
| Drying | ||
| Drying Temperature | 130 – 140°C | |
| Drying Time | 4 – 6 hours | |
| Maximum Moisture Content | ≤0.02% | |
| Injection Molding | ||
| Melt Temperature | 340 – 380°C | |
| Front Zone 3 Temperature | 350 – 370°C | |
| Middle Zone 2 Temperature | 345 – 365°C | |
| Mold Temperature | — | |
| Vent Depth | 0.025 – 0.076 mm | |
| Shot to Cylinder Size | 40 – 60% |
Critical Processing Warnings:
-
Internal Mold Release: This grade contains internal mold release agents for improved demolding and processing efficiency.
-
Drying: ULTEM ATX200R is hygroscopic and must be dried to <0.02% moisture before processing. Dry at 130-140°C for 4-6 hours.
-
High Flow: This grade offers high flow characteristics (MVR 16 cm³/10min) for easier processing and better mold filling of complex, thin-walled parts.
-
Melt Temperature: Recommended melt temperature range is 340-380°C. Avoid excessive residence times to prevent thermal degradation.
-
Gate Design: Use large gates and runners to minimize flow resistance and reduce molded-in stress.
-
Regrind: Regrind can be used up to 20-25% with virgin material, provided it is clean and properly dried.
Related Products
-
Explore PEI / Polyetherimide – Browse all ULTEM PEI resin options
-
Explore Engineering Plastics – Browse all engineering plastic materials
-
About Our Company – Learn more about our supply capabilities and quality assurance
Technical Documents
| Document Type | Description & Source |
|---|---|
| SABIC Official TDS | Complete physical, thermal, and mechanical properties of ULTEM ATX200R |
| SABIC Official SDS | GHS-compliant chemical safety documentation |
| UL Yellow Card | UL certification E45329-100397331 |
| COA (Certificate of Analysis) | Batch-specific quality certification |
| Processing Guide | Detailed processing guidelines for ULTEM resins |
Request any document above by:
-
Email:
ruiqingchem@gmail.com -
Online form: Our contact page
We reply within one working business day. Please clearly state product (ULTEM ATX200R) and document type you require.
FAQ
Q1: What is ULTEM ATX200R and what is it used for?
A: ULTEM ATX200R is a high flow, unreinforced polyetherimide (PEI) blend manufactured by SABIC. It combines high impact resistance, flame retardancy (UL94 V-0), and internal mold release for improved demolding efficiency. It is widely used in automotive, aerospace, electrical components, consumer goods, drones, healthcare, and industrial applications.
Q2: What is the difference between ULTEM ATX200 and ATX200R?
A: The key difference is that ATX200R includes internal mold release for improved demolding and processing efficiency. ATX200 does not have internal mold release. Both grades share similar high flow, high impact, and flame retardant properties.
Q3: What is the difference between ULTEM ATX200R and ATX200F?
A: ATX200F is US FDA food contact compliant, while ATX200R features internal mold release. ATX200R does not carry FDA food contact certification. Choose ATX200R for improved demolding efficiency; choose ATX200F for food contact applications.
Q4: What flame retardant rating does ULTEM ATX200R have?
A: ULTEM ATX200R is rated UL94 V-0. It is non-halogenated flame retardant.
Q5: What is the glass transition temperature of ULTEM ATX200R?
A: The glass transition temperature (Tg) is approximately 210°C.
Q6: What is the density of ULTEM ATX200R?
A: The density is 1.26 g/cm³.
Q7: Is ULTEM ATX200R PFAS-free?
A: Yes. ULTEM ATX200R has no PFAS intentionally added during manufacturing.
Q8: What is the melt flow rate of ULTEM ATX200R?
A: The Melt Flow Rate (MFR) is 26.5 g/10min at 337°C, 6.6kg; the Melt Volume Rate (MVR) is 16 cm³/10min at 340°C, 5kg.
Q9: What processing methods can be used for ULTEM ATX200R?
A: ULTEM ATX200R is processed by injection molding.
Q10: What is the tensile strength of ULTEM ATX200R?
A: Tensile yield strength is 95-96 MPa; tensile break strength is 75-85 MPa.
Q11: What is the tensile modulus of ULTEM ATX200R?
A: The tensile modulus is 3,000-3,300 MPa.
Q12: What is the shrinkage of ULTEM ATX200R?
A: Mold shrinkage (flow, 3.2mm) is 0.50-0.70%.
Q13: Can ULTEM ATX200R be custom colored?
A: Yes. ULTEM ATX200R is opaque and all colors are customizable via SABIC‘s ColorXpress service.
Q14: What is the UL RTI of ULTEM ATX200R?
A: The UL Relative Thermal Index (Elec/Imp/Str) is 115°C.
Q15: What is the lead time for orders?
A: Regular orders ship within 7-10 working days after payment confirmation. Large-volume or urgent orders can be negotiated separately.
CTA (Call to Action)
Ready to order ULTEM ATX200R?
To get a precise quotation and professional technical support, please share:
-
Required quantity (kg)
-
Destination port or delivery address
-
Target application (automotive, aerospace, electrical, drone, healthcare, etc.)
-
Processing method (injection molding)
-
Color requirement (custom colors available via ColorXpress)
-
Document requirement (TDS, SDS, UL, COA, etc.)
Sample Policy:
-
Samples are for laboratory validation tests only, not for production use.
-
Buyer bears international sample-shipping freight.
-
If bulk-product performance deviates from sample reference, SABIC official TDS serves as the authoritative benchmark.
Take action now:
-
📧 Email Us –
ruiqingchem@gmail.com -
📝 Send Inquiry – Use our quick inquiry form
-
💬 Live Chat – Click the bottom-right chat widget to speak directly with our team
After-Sales Support
| Service | Details |
|---|---|
| Quality Inspection Period | All quality-related claims must be submitted within 7 working-days after delivery, supported by test data and photographic evidence. |
| Return / Exchange Policy | Confirmed product defects caused by our side trigger replacement or refund. Terms and conditions apply. |
| Logistics Damage | Report shipping damage directly to carrier immediately upon goods receipt. We assist with claim-document preparation. |
| Technical Support | Remote technical guidance available. On-site troubleshooting can be arranged upon special request. |
| Export Documentation | We supply commercial invoice, packing list, bill of lading, COA, and additional compliance certificates (e.g., UL, RoHS) on request. |
Disclaimer
DISCLAIMER: All technical data is referenced from original SABIC typical values for ULTEM ATX200R. Our company acts as authorized distributor/trader rather than original manufacturer. Final performance depends on processing conditions, mold design, and part geometry. Buyers shall independently validate product suitability for individual applications. Our firm bears no liability for product failure caused by improper processing or improper usage. Always reference the latest SABIC official TDS of ULTEM ATX200R as the definitive specification.