Micromax 0020L 100 Ohm High Productivity Resistor Paste
Type: Chip Resistor Paste
Pack: 100G / 1000G
Viscosity: 150-240 Pa.s
Resistivity: 100 Ω/sq
Firing: 850°C / 30 min
Shelf Life: 6 months
Micromax 0020L delivers 100 Ω/sq high resistance performance with high productivity and excellent printability — engineered for high yield chip resistor manufacturing with tight resistance distribution and 850°C fast firing.
Micromax 0020L is a high productivity thick film paste engineered for chip resistor production requiring 100 Ω/sq resistivity and consistent manufacturing yields. Formulated to deliver tight resistance distribution with balanced cost vs TCR performance, this grade supports high-volume manufacturing while maintaining stable electrical properties across production batches. The material offers excellent blendability with adjacent members including 003XZ (1kΩ/sq) for resistance tuning flexibility.
This resistor paste is optimized for high-resolution screen printing and is compatible with multiple termination systems including Micromax 5426, 5421E, 5418 Ag/Pd, and 5463 Ag pastes. It supports co-firing at 850°C peak temperature with a 30-minute total cycle for efficient production throughput. The cadmium-free, nickel-free and phthalate-free formulation meets international environmental standards including RoHS and REACH. Standard packaging options are 100G and 1000G.
Genuine Micromax Imported Stock and Technical Support
We maintain stable inventory of authentic Micromax 0020L 100 ohm high productivity resistor paste. Factory-original TDS and batch-specific COA can be provided upon request for electronic component manufacturing projects.
Request Sample, TDS & Quotation
Complete TDS, COA, and regulatory documentation available
Core Advantages of Micromax 0020L
- 100 Ω/sq high resistance formulation — precise high-resistance chip resistor applications
- High productivity — designed for high-volume manufacturing with consistent yields
- Balanced cost vs TCR performance — optimal trade-off for commercial resistor production
- Tight resistance distribution — reliable electrical performance across production runs
- Excellent blendability — adjustable resistance range with 003XZ (1kΩ/sq) and other grades
- Excellent printability — optimized for 250-325 mesh screens at 14-16 μm dried thickness
- Insensitive to firing profile and chip size — robust manufacturing performance
- RoHS, REACH compliant; Cadmium/Nickel/Phthalate free — satisfies global environmental regulations
Main Applications
- Chip Resistors — high resistance chip resistor mass production
- Hybrid Circuits — resistor networks requiring high resistance values
- Surface Mount Devices — SMD resistor components for consumer and industrial electronics
- Automotive Electronics — resistor components requiring high resistance and thermal stability
Full Technical Parameters
| Property | Typical Value | Test / Reference |
| Product Type | Thick film chip resistor paste | — |
| Application | Chip resistor manufacturing | — |
| Packaging Specification | 100G, 1000G | Standard packing |
| Resistivity | 100 Ω/sq | Standard geometry |
| Viscosity (Brookfield HAT 10 rpm) | 150-240 Pa.s | SC4-14/6R, 25°C |
| Recommended Mesh | 250-325 mesh | — |
| Emulsion Thickness | 10-15 μm | — |
| Dried Film Thickness | 14-16 μm | Recommended range |
| Leveling Time | 5-10 min | Room temperature |
| Drying Temperature | 150°C | 10-15 minutes |
| Firing Peak Temperature | 850°C | 10 min at peak, 30 min total |
| Termination Compatibility | Micromax 5426, 5421E, 5418 Ag/Pd, 5463 Ag | — |
| Substrate Compatibility | 96% alumina | — |
| Blendability | Linear blend behavior with 003XZ (1kΩ/sq) | — |
| Environmental Compliance | RoHS, REACH, Cadmium free, Nickel free, Phthalate free | — |
| Shelf Life | 6 months in unopened containers | — |
| Storage Temperature | 5-30°C | — |
Note: All listed values are typical and may vary by batch. Independent qualification testing is required prior to production use.
Recommended Processing Conditions
| Parameter | Recommended Value |
| Screen Mesh | 250-325 mesh |
| Emulsion Thickness | 10-15 μm |
| Dried Film Thickness | 14-16 μm |
| Leveling Time | 5-10 minutes |
| Drying Temperature | 150°C |
| Drying Time | 10-15 minutes |
| Firing Peak Temperature | 850°C |
| Total Firing Cycle | 30 minutes (10 min at peak) |
| Substrate | 96% alumina |
Handling and Storage Recommendations
| Storage Rules | Store in tightly sealed containers in clean, stable environment at 5-30°C. |
| Shelf Life | 6 months in unopened containers from date of shipment. |
| Pre-use Preparation | Thoroughly mix prior to use. Some settling may occur. |
| Thinning | Not normally required; use Micromax 8250(T) thinner sparingly for evaporative losses. |
Official Technical Documentation
| Document Type | Document Introduction | Document Request |
| TDS | Micromax 0020L original factory technical data sheet | Request TDS |
| COA | Batch-specific certificate of analysis | Request COA |
| SDS | Safety Data Sheet for handling and storage | Request SDS |
Frequently Asked Questions
What is Micromax 0020L?
Micromax 0020L is a high productivity thick film paste delivering 100 Ω/sq resistivity for chip resistor applications. It combines balanced cost vs TCR performance, tight resistance distribution, and excellent blendability for reliable resistor production.
What is the resistivity of Micromax 0020L?
Micromax 0020L provides a fixed resistivity of 100 Ω/sq, suitable for high resistance chip resistor manufacturing.
What is the viscosity of Micromax 0020L?
This paste exhibits viscosity in the range of 150-240 Pa.s when measured with Brookfield HAT at 10 rpm, SC4-14/6R spindle, 25°C.
What is the recommended processing profile for Micromax 0020L?
Recommended processing: level for 5-10 minutes, dry at 150°C for 10-15 minutes, then fire at 850°C peak for 10 minutes within a 30-minute total cycle.
What is the recommended dried film thickness for Micromax 0020L?
Micromax 0020L is optimized for 14-16 μm dried film thickness using 250-325 mesh screens with 10-15 μm emulsion.
Is Micromax 0020L environmentally compliant?
Yes. Micromax 0020L contains no intentionally added cadmium, nickel or phthalates, meeting RoHS and REACH environmental standards.
What terminations are compatible with Micromax 0020L?
Micromax 0020L is compatible with high silver terminations including Micromax 5426, 5421E, 5418 Ag/Pd, and 5463 Ag termination pastes.
What packaging sizes are available for Micromax 0020L?
Micromax 0020L is supplied in 100G and 1000G containers. For larger volume requirements, please contact our sales team.
Get Micromax 0020L Bulk Pricing and Technical Support
We supply genuine Micromax 0020L 100 ohm high productivity resistor paste for electronic component manufacturing. Contact us for bulk pricing, sample availability, technical documents, and application support.
Inquire Bulk Price & Technical Support
Disclaimer: All technical data on this page are for general guidance only and are not product specifications. Buyers must carry out independent trials and verify suitability before bulk ordering. Actual values may vary between production lots.