Micromax 0011Z High Power Stability Chip Resistor Paste
Type: Chip Resistor Paste
Pack: 100G / 1000G
Viscosity: 110-180 Pa.s
Firing: 850°C / 30 min
Laser: High Speed Trimmable
Shelf Life: 6 months
Micromax 0011Z delivers excellent power handling stability with exceptional ESD stability and low noise performance — engineered for small sized chip resistor applications with high speed laser trimmability and 850°C fast firing.
Micromax 0011Z is a high power stability thick film paste specifically developed for chip resistor applications where power handling, ESD protection, and noise performance are critical. This grade delivers excellent power handling stability to withstand demanding operating conditions, exceptional ESD stability for sensitive circuit designs, and low noise performance meeting MIL-STD-202 standards. The material maintains consistent performance even with thinner thickness and smaller chip sizes.
This resistor paste offers high speed laser trimmability for precise resistance adjustment, enabling tight tolerance manufacturing. It provides excellent blendability with both lower and higher ohm Micromax 00X1 resistor members, achieving good linearity across a wide resistance range from 70mΩ to 10MΩ. The formulation is insensitive to firing profile and chip size variations, supporting consistent production yields. It is compatible with Micromax 5426 and 5421E Ag/Pd terminations. The cadmium-free, nickel-free and phthalate-free formulation meets international environmental standards including RoHS and REACH. Standard packaging options are 100G and 1000G.
Genuine Micromax Imported Stock and Technical Support
We maintain stable inventory of authentic Micromax 0011Z high power stability chip resistor paste. Factory-original TDS and batch-specific COA can be provided upon request for electronic component manufacturing projects.
Request Sample, TDS & Quotation
Complete TDS, COA, and regulatory documentation available
Core Advantages of Micromax 0011Z
- Excellent power handling stability — reliable performance under demanding power conditions
- Exceptional ESD stability — robust electrostatic protection for sensitive applications
- High speed laser trimmable — precise resistance adjustment for tight tolerance manufacturing
- Low noise performance — meets MIL-STD-202 standards for signal integrity
- Excellent thin thickness & small chip performance — consistent properties with miniaturized designs
- Wide blendability range — linear blending across 70mΩ to 10MΩ resistance range
- Insensitive to firing profile & chip size — robust manufacturing performance
- RoHS, REACH compliant; Cadmium/Nickel/Phthalate free — satisfies global environmental regulations
Main Applications
- Chip Resistors — small sized chip resistor manufacturing
- Hybrid Circuits — resistor networks requiring power handling and low noise
- Surface Mount Devices — SMD resistor components for compact electronics
- Automotive Electronics — resistor components requiring power stability and ESD protection
- Precision Measurement Equipment — low noise, tight tolerance resistor applications
Full Technical Parameters
| Property | Typical Value | Test / Reference |
| Product Type | Thick film chip resistor paste | — |
| Application | Chip resistor manufacturing | — |
| Packaging Specification | 100G, 1000G | Standard packing |
| Viscosity (Brookfield HAT 10 rpm) | 110-180 Pa.s | SC4-14/6R, 25°C |
| Recommended Mesh | 250-325 mesh | — |
| Emulsion Thickness | 10-15 μm | — |
| Dried Film Thickness | 14-16 μm | Recommended range |
| Leveling Time | 5-10 min | Room temperature |
| Drying Temperature | 150°C | 10-15 minutes |
| Firing Peak Temperature | 850°C | 10 min at peak, 30 min total |
| Power Handling Stability | Excellent | — |
| ESD Stability | Exceptional | — |
| Noise Performance | Low noise (MIL-STD-202) | — |
| Laser Trimmability | High speed laser trimmable | — |
| Blendability Range | 70mΩ to 10MΩ | — |
| Termination Compatibility | Micromax 5426, 5421E Ag/Pd | — |
| Substrate Compatibility | 96% alumina | — |
| Environmental Compliance | RoHS, REACH, Cadmium free, Nickel free, Phthalate free | — |
| Shelf Life | 6 months in unopened containers | — |
| Storage Temperature | 5-30°C | — |
Note: All listed values are typical and may vary by batch. Independent qualification testing is required prior to production use.
Recommended Processing Conditions
| Parameter | Recommended Value |
| Screen Mesh | 250-325 mesh |
| Emulsion Thickness | 10-15 μm |
| Dried Film Thickness | 14-16 μm |
| Leveling Time | 5-10 minutes |
| Drying Temperature | 150°C |
| Drying Time | 10-15 minutes |
| Firing Peak Temperature | 850°C |
| Total Firing Cycle | 30 minutes (10 min at peak) |
| Substrate | 96% alumina |
Handling and Storage Recommendations
| Storage Rules | Store in tightly sealed containers in clean, stable environment at 5-30°C. |
| Shelf Life | 6 months in unopened containers from date of shipment. |
| Pre-use Preparation | Thoroughly mix prior to use. Some settling may occur. |
| Thinning | Not normally required; use Micromax 8250(T) thinner sparingly for evaporative losses. |
Official Technical Documentation
| Document Type | Document Introduction | Document Request |
| TDS | Micromax 0011Z original factory technical data sheet | Request TDS |
| COA | Batch-specific certificate of analysis | Request COA |
| SDS | Safety Data Sheet for handling and storage | Request SDS |
Frequently Asked Questions
What is Micromax 0011Z?
Micromax 0011Z is a high power stability thick film paste designed for small sized chip resistor production. It combines excellent power handling, exceptional ESD protection, low noise, and high speed laser trimmability for precision resistor manufacturing.
What is the viscosity of Micromax 0011Z?
Micromax 0011Z exhibits a viscosity between 110 and 180 Pa.s when measured with Brookfield HAT at 10 rpm, SC4-14/6R spindle, 25°C.
What is the recommended processing profile for Micromax 0011Z?
Recommended processing: level for 5-10 minutes, dry at 150°C for 10-15 minutes, then fire at 850°C peak for 10 minutes within a 30-minute total cycle.
What is the recommended dried film thickness for Micromax 0011Z?
Micromax 0011Z is optimized for 14-16 μm dried film thickness using 250-325 mesh screens with 10-15 μm emulsion.
Can Micromax 0011Z be laser trimmed?
Yes. Micromax 0011Z supports high speed laser trimming for precise resistance adjustment, enabling tight tolerance chip resistor manufacturing.
Is Micromax 0011Z environmentally compliant?
Yes. Micromax 0011Z contains no intentionally added cadmium, nickel or phthalates, meeting RoHS and REACH environmental standards.
What terminations are compatible with Micromax 0011Z?
Micromax 0011Z is compatible with high silver terminations, with reported properties obtained using Micromax 5426 Ag/Pd termination and 5421E Ag/Pd conductor.
What packaging sizes are available for Micromax 0011Z?
Micromax 0011Z is supplied in 100G and 1000G containers. For larger volume requirements, please contact our sales team.
Get Micromax 0011Z Bulk Pricing and Technical Support
We supply genuine Micromax 0011Z high power stability chip resistor paste for electronic component manufacturing. Contact us for bulk pricing, sample availability, technical documents, and application support.
Inquire Bulk Price & Technical Support
Disclaimer: All technical data on this page are for general guidance only and are not product specifications. Buyers must carry out independent trials and verify suitability before bulk ordering. Actual values may vary between production lots.