Fortron 6162A7 is a 60% mineral and glass fiber reinforced polyphenylene sulfide (PPS) injection molding grade from Celanese Corporation, available in black color. This grade features excellent flow characteristics combined with a Comparative Tracking Index (CTI) of 225V , making it particularly suitable for complex electronic and automotive components requiring good electrical tracking resistance .
The 60% mineral/glass reinforcement provides exceptional stiffness, dimensional stability, and low warpage. The high flow capability enables the molding of intricate parts with long flow paths and thin walls while maintaining the superior mechanical and thermal properties characteristic of PPS .
As a linear, semi-crystalline PPS, Fortron 6162A7 exhibits excellent chemical resistance to solvents, acids, bases, and automotive fuels below 200°C . It provides high continuous use temperature (160°C to 240°C), very low moisture absorption (0.017%), and inherent V-0 flame retardancy at 0.8mm thickness .
For more PPS grades and technical information, please visit our PPS/Polyphenylene Sulfide product page. You can also explore Celanese’s official Fortron PPS portfolio for additional manufacturer insights.
Key Features of Fortron 6162A7
-
60% Mineral/Glass Reinforcement – Exceptional stiffness and dimensional stability
-
Excellent Flow – High flow for complex injection molded parts
-
Black Color – Pre-colored black for aesthetic and functional applications
-
High CTI (225V) – Enhanced tracking resistance for high-voltage applications
-
High Stiffness – Tensile modulus of 15,400 MPa; flexural modulus of 14,500 MPa
-
High Strength – Tensile strength of 115 MPa; flexural strength of 185 MPa
-
Excellent Heat Resistance – HDT of 270°C at 1.80 MPa; melting temperature 280°C
-
Inherent Flame Retardancy – V-0 at 0.8mm and 1.5mm thickness
-
Excellent Chemical Resistance – Resists solvents, acids, bases, and automotive fuels below 200°C
-
Very Low Moisture Absorption – 0.017% water absorption
-
Regulatory Compliance – RoHS compliant
-
Global Supply – Available across North America, Europe, Asia Pacific, Latin America, Africa & Middle East
Typical Applications for Fortron 6162A7
| Industry | Typical Components & Considerations |
|---|---|
| Automotive | Under-the-hood components, electronic housings, connectors – requiring chemical resistance and heat stability |
| Electrical & Electronics | Relays, connectors, coil bobbins, sensors – requiring V-0 flammability, CTI 225V, and high flow |
| 家电部件 | Appliance components – requiring heat resistance and flame retardancy |
| 复杂注塑件 | Parts with long flow paths and thin walls – utilizing high flow characteristics |
| Metal Replacement | Applications requiring metal replacement with high-performance polymer |
Typical Properties of Fortron 6162A7
| Property | Value | Test Method |
|---|---|---|
| Physical | ||
| Density | 1.92 g/cm³ | ISO 1183 |
| Water Absorption (Saturation) | 0.017% | ISO 62 |
| Molding Shrinkage – Flow | 0.10 – 0.30% | ISO 294-4 |
| Molding Shrinkage – Transverse | 0.40 – 0.80% | ISO 294-4 |
| Mechanical | ||
| Tensile Modulus | 15,400 MPa | ISO 527-2/1A/1 |
| Tensile Strength at Break | 115 MPa | ISO 527-2/1A/5 |
| Tensile Strain at Break | 1.3% | ISO 527-2/1A/5 |
| Flexural Modulus | 14,500 MPa | ISO 178 |
| Flexural Strength | 185 MPa | ISO 178 |
| Impact | ||
| Charpy Notched Impact (23°C) | 4.5 kJ/m² | ISO 179/1eA |
| Izod Notched Impact (23°C) | 6.0 kJ/m² | ISO 180/1A |
| Thermal | ||
| Melting Temperature | 280°C | ISO 11357-3 |
| Glass Transition Temperature | 90°C | ISO 11357-2 |
| HDT @ 1.80 MPa | 270°C | ISO 75-2/A |
| HDT @ 8.00 MPa | 215°C | ISO 75-2/C |
| CTE – Flow | 1.9 × 10⁻⁵/K | ISO 11359-2 |
| CTE – Transverse | 3.4 × 10⁻⁵/K | ISO 11359-2 |
| Electrical | ||
| Comparative Tracking Index (CTI) | 225 V | IEC 60112 |
| Relative Permittivity (1MHz) | 5.68 | IEC 60250 |
| Dissipation Factor (1MHz) | 1.0 × 10⁻³ | IEC 60250 |
| Flammability | ||
| Flammability @ 0.8mm | V-0 | UL 94 |
| Flammability @ 1.5mm | V-0 | UL 94 |
Important Notes on Typical Data
📌 Values are typical – The data listed above is sourced from manufacturer data sheets for reference only and does not constitute binding product specifications for Fortron 6162A7 .
📌 Batch variations – Batch-to-batch deviations may exist. For critical applications, validate performance with batch-specific COA certificates.
📌 Final performance – Actual performance depends on processing conditions and part design. Refer to ISO testing standards for detailed methodology.
📌 Authoritative reference – The manufacturer’s official TDS shall serve as the definitive technical reference for Fortron 6162A7. Request the latest official TDS from our sales team.
Processing Guidelines for Fortron 6162A7
| Step | Process |
|---|---|
| Processing Methods | Injection Molding |
| Drying Recommended | Yes |
| Drying Temperature | 130 – 140°C |
| Drying Time | 3 – 4 hours |
| Suggested Max Moisture | ≤ 0.02% |
| Melt Temperature Range | 320 – 340°C |
| Mold Temperature | 140 – 160°C |
| Hold Pressure | 30 – 70 MPa |
| Storage | Store in original, sealed packaging in a cool, dry place away from direct sunlight |
Critical Processing Warnings for Fortron 6162A7
⚠️ Drying Requirement – Fortron 6162A7 requires drying prior to processing. Predrying in a dehumidified air dryer at 130–140°C for 3–4 hours is recommended. The time between drying and processing should be as short as possible.
⚠️ Moisture Control – Maximum residual moisture content should be ≤ 0.02%. Proper drying is essential to prevent void formation and ensure optimal part quality.
⚠️ Melt Temperature – The recommended melt temperature range is 320–340°C. Avoid exceeding 340°C to prevent material degradation.
⚠️ High Flow Characteristics – This grade features excellent flow, enabling the molding of complex parts with long flow paths. Adjust processing parameters accordingly to optimize fill and reduce pressure requirements .
⚠️ High Filler Content – With 60% mineral/glass reinforcement and a density of 1.92 g/cm³, this grade requires consideration for equipment wear and proper screw design.
⚠️ Black Color – This grade is pre-colored black. Check color consistency across batches for aesthetic applications .
⚠️ Storage – Store in original, sealed packaging in a cool, dry place away from direct sunlight. For subsequent storage, the material should be stored dry until processed.
Comparison: Fortron 6162A7 vs. Fortron 6160B4 vs. Fortron 4665B6
| Feature | Fortron 6162A7 | Fortron 6160B4 | Fortron 4665B6 |
|---|---|---|---|
| Filler Content | 60% Mineral/Glass | 60% Mineral/Glass | 65% Mineral/Glass |
| Key Feature | High flow + Black + CTI 225V | Superior contact corrosion resistance | High CTI (250), very low warpage |
| Tensile Modulus | 15,400 MPa | 17,300 MPa | 17,300 MPa |
| Tensile Strength | 115 MPa | 145 MPa | 110-125 MPa |
| HDT @ 1.80 MPa | 270°C | 270°C | 270°C |
| CTI | 225 V | 175 | 250 |
| Density | 1.92 g/cm³ | 1.90 g/cm³ | 2.03 g/cm³ |
| Appearance | Black | Black | Gray/Black |
| Primary Application | High-flow, black, CTI 225V applications | Electronic components, contact corrosion | High-voltage electronics |
Related Products
-
PPS/Polyphenylene Sulfide – View our full range of PPS products
-
Fortron 6160B4 – 60% mineral/glass reinforced PPS with superior contact corrosion resistance
-
Fortron 4665B6 – 65% mineral/glass reinforced PPS with high CTI (250)
-
Fortron 6150T4 – 50% glass/mineral reinforced, impact modified PPS
-
Explore Engineering Plastics – Browse all engineering plastic materials
-
About Our Company – Learn more about our supply capabilities and quality assurance
Technical Documents for Fortron 6162A7
| Document Type | Description & Source |
|---|---|
| Manufacturer Official TDS | Complete physical, thermal, and mechanical properties of Fortron 6162A7 |
| Manufacturer Official SDS | GHS-compliant safety documentation |
| COA (Certificate of Analysis) | Batch-specific quality certification for Fortron 6162A7 |
| UL Yellow Card | UL safety certification (E107854) |
Request any document above by:
📧 Email: ruiqingchem@gmail.com
📝 Online form: Our contact page
We reply within one working business day. Please clearly state product (Fortron 6162A7) and document type you require.
FAQ about Fortron 6162A7
Q1: What is Fortron 6162A7?
A: Fortron 6162A7 is a 60% mineral and glass fiber reinforced PPS injection molding grade from Celanese, available in black color with excellent flow and CTI 225V .
Q2: What are the key features of Fortron 6162A7?
A: 60% mineral/glass reinforcement; high flow; black color; CTI 225V; tensile modulus 15,400 MPa; HDT 270°C; V-0 at 0.8mm; excellent chemical resistance .
Q3: What are the typical applications for Fortron 6162A7?
A: Automotive under-the-hood components, electronic components (relays, connectors, sensors), appliance parts, and complex injection molded parts .
Q4: What is the recommended drying condition for Fortron 6162A7?
A: Dry at 130–140°C for 3–4 hours using a dehumidified air dryer. Maximum residual moisture should be ≤ 0.02%.
Q5: What is the density of Fortron 6162A7?
A: 1.92 g/cm³ .
Q6: What is the HDT @ 1.80 MPa of Fortron 6162A7?
A: 270°C .
Q7: What regions is Fortron 6162A7 available in?
A: North America, Europe, Asia Pacific, Latin America, Africa & Middle East .
Q8: Is Fortron 6162A7 flame retardant?
A: Yes, V-0 at 0.8mm and 1.5mm thickness (UL 94) .
Q9: What is the CTI of Fortron 6162A7?
A: 225 V (IEC 60112) .
Q10: What color is Fortron 6162A7?
A: Black .
Q11: What is the difference between Fortron 6162A7 and Fortron 6160B4?
A: Both have 60% mineral/glass reinforcement. Fortron 6162A7 features high flow, black color, and CTI 225V, while Fortron 6160B4 is designed for superior contact corrosion resistance with CTI 175.
Q12: Is Fortron 6162A7 RoHS compliant?
A: Yes, it complies with RoHS regulations.
CTA (Call to Action)
Ready to order Fortron 6162A7?
To get a precise quotation and professional technical support for Fortron 6162A7, please share:
-
Required quantity (kg)
-
Destination port or delivery address
-
Target application (automotive, electronics, appliance, complex molding, etc.)
-
Document requirements (TDS, SDS, COA, UL docs)
Sample Policy:
-
Samples of Fortron 6162A7 are for laboratory validation tests only, not for production use.
-
Buyer bears international sample-shipping freight.
-
If bulk-product performance deviates from sample reference, the manufacturer’s official TDS serves as the authoritative benchmark.
Take action now:
📧 Email Us – ruiqingchem@gmail.com
📝 Send Inquiry – Use our quick inquiry form
💬 Live Chat – Click the bottom-right chat widget to speak directly with our team
After-Sales Support
| Service | Details |
|---|---|
| Quality Inspection Period | All quality-related claims must be submitted within 7 working days after delivery, supported by test data and photographic evidence. |
| Return / Exchange Policy | Confirmed product defects caused by our side trigger replacement or refund. Terms and conditions apply. |
| Logistics Damage | Report shipping damage directly to carrier immediately upon goods receipt. We assist with claim-document preparation. |
| Technical Support | Remote technical guidance available. On-site troubleshooting can be arranged upon special request. |
| Export Documentation | We supply commercial invoice, packing list, bill of lading, COA, and additional compliance certificates on request. |
Disclaimer
DISCLAIMER: All technical data is referenced from original manufacturer typical values for Fortron 6162A7 . Our company acts as supplier/trader rather than original manufacturer. Final performance depends on processing conditions and part design. Buyers shall independently validate product suitability for individual applications. Our firm bears no liability for product failure caused by improper processing or improper usage. Always reference the latest manufacturer official TDS of Fortron 6162A7 as the definitive specification.