描述
NORYL SE1GFN2 Resin is a 20% glass fiber reinforced blend of polyphenylene ether (PPE) and polystyrene (PS), manufactured by SABIC . This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 2mm and V-1 at 1.5mm, along with a UL746C Outdoor Suitability rating of F1 and RTI of 110°C . UL Yellow Card: E121562-624509 .
NORYL SE1GFN2 exhibits high heat resistance, good dielectric strength, dimensional stability, hydrolytic stability, and very low moisture absorption . The 20% glass reinforcement provides high stiffness and strength while maintaining low warpage, low shrinkage, and low specific gravity . This grade is PFAS-free (AMR and EUR sourced only) and commercially active in the Americas and Asia Pacific . Physical property data is determined using test methods established by UL, the globally recognized safety certification organization.
For more NORYL grades and technical information, please visit our PPO/PPE product page.
Key Features of NORYL SE1GFN2 Resin
-
20% Glass Fiber Reinforced – Provides enhanced stiffness, strength, and dimensional stability
-
Halogen-Free Flame Retardant – Non-brominated, non-chlorinated flame retardant system
-
UL94 5VA & V-1 Rated – 5VA at 2mm; V-1 at 1.5mm
-
UL746C F1 Outdoor Suitability – Suitable for outdoor exposure with UV and weather resistance
-
High Heat Resistance – RTI of 110°C
-
Good Dielectric Strength – Strong electrical performance for demanding applications
-
High Stiffness – Flexural modulus of 5,500–5,600 MPa (ASTM/ISO)
-
High Strength – Tensile strength at break of 106–120 MPa
-
Good Impact Resistance – Notched Izod impact of 100 J/m at 23°C
-
Low Warpage & Dimensional Stability – Low shrinkage and low warpage
-
Very Low Moisture Absorption – Maintains properties in humid environments
-
Hydrolytic Stability – Resists degradation in wet environments
-
Low Specific Gravity – Lightweight for various applications
-
Amorphous – Low shrinkage characteristics
-
PFAS-Free – No PFAS intentionally added (AMR and EUR sourced only)
-
RoHS Compliant – Meets global environmental standards
-
Injection Moldable – Suitable for standard injection molding processes
Typical Applications for NORYL SE1GFN2 Resin
| Industry | Typical Components & Considerations |
|---|---|
| Renewable Energy | Solar frames – UL746C F1 outdoor rating, weatherability, dimensional stability |
| Power Systems | Unattended power supply (UPS) inverter/charger – flame retardant, high heat resistance |
| Electrical & Electronics | Indoor and outdoor electrical enclosures, housings, connectors – UL94 5VA/V-1, UL746C F1 |
| Building & Construction | Wall plates, sockets, switches – flame retardant, dimensional stability, low warpage |
| Automotive EV | Electric vehicle components, battery applications – high heat resistance, hydrolytic stability |
| Energy Management | Energy management applications – flame retardant, electrical performance |
| Consumer Electronics | Mobile phones, computers, tablets – thin-wall capability, dimensional stability |
| Drones | Drone components – lightweight, flame retardant, dimensional stability |
Typical Properties of NORYL SE1GFN2 Resin
| Property | Value | Test Method |
|---|---|---|
| Physical | ||
| Density / Specific Gravity | ~1.16 g/cm³ (1160 kg/m³) | ASTM D792 |
| Water Absorption (24 hrs) | 0.06% | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.3 – 0.5% | SABIC Method |
| Mechanical (ASTM) | ||
| Tensile Stress at Break (Type I, 5 mm/min) | 106 – 120 MPa | ASTM D638 |
| Tensile Strain at Break (Type I, 5 mm/min) | 3 – 5% | ASTM D638 |
| Tensile Modulus (5 mm/min) | 7,100 MPa | ASTM D638 |
| Flexural Stress, Yield (1.3 mm/min, 50 mm span) | 140 MPa | ASTM D790 |
| Flexural Modulus (1.3 mm/min, 50 mm span) | 5,500 MPa | ASTM D790 |
| Hardness, Rockwell L | 106 | ASTM D785 |
| Impact (ASTM) | ||
| Notched Izod Impact (23°C) | 100 – 106 J/m | ASTM D256 |
| Notched Izod Impact (-40°C) | 96 J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 520 J/m | ASTM D4812 |
| Instrumented Dart Impact Total Energy (23°C) | 18 J | ASTM D3763 |
| Mechanical (ISO) | ||
| Tensile Stress at Break (50 mm/min) | 100 MPa | ISO 527 |
| Tensile Strain at Break (50 mm/min) | 2.5% | ISO 527 |
| Tensile Modulus (1 mm/min) | 6,400 MPa | ISO 527 |
| Flexural Stress, Yield (2 mm/min) | 150 MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 5,600 MPa | ISO 178 |
| Izod Impact, Unnotched (23°C, 80×10×4) | 28 kJ/m² | ISO 180/1U |
| Thermal | ||
| HDT, 1.82 MPa (6.4mm, unannealed) | Refer to full TDS | ASTM D648 |
| Vicat Softening Temperature | Refer to full TDS | ASTM D1525 |
| UL RTI Electrical | 110°C | UL 746B |
| UL RTI Mechanical with Impact | 105°C | UL 746B |
| UL RTI Mechanical without Impact | 110°C | UL 746B |
| Electrical (ASTM) | ||
| Arc Resistance | 60 – 119 s (Tungsten) | ASTM D495 |
| Comparative Tracking Index (CTI) | 400 – 599 V | UL 746A |
| High Amp Arc Ignition (HAI) | 30 – 59 (At =1.5 mm) | UL 746A |
| Dielectric Strength (in oil) | 23.6 kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 2.98 | ASTM D150 |
| Dissipation Factor (60 Hz) | 0.0016 | ASTM D150 |
| Flammability | ||
| Flame Rating (2.0mm) | 5VA | UL 94 |
| Flame Rating (1.5mm) | V-1 | UL 94 |
| Flame Rating (6.0mm) | V-0 | IEC 60695-11-10 |
| UL746C Outdoor Suitability | F1 | UL 746C |
| Glow Wire Flammability Index (GWFI) | 960°C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (GWIT) | 775°C | IEC 60695-2-13 |
| UL Yellow Card | E121562-624509 | UL |
| Processing | ||
| Drying Temperature | 105 – 110°C | SABIC Method |
| Drying Time | 3 – 4 hours | SABIC Method |
| Maximum Moisture Content | < 0.02% | SABIC Method |
| Melt Temperature | 300 – 325°C | SABIC Method |
| Mold Temperature | 80 – 110°C | SABIC Method |
Important Notes on Typical Data:
Values listed are typical and sourced from manufacturer data sheets. They do not constitute binding product specification.
Batch-to-batch deviations may exist. For critical applications, validate performance with batch-specific COA certificate.
Final performance depends on processing conditions and part design.
Manufacturer official TDS shall serve as definitive technical reference. Request the latest official TDS from our sales team.
Processing Guidelines for NORYL SE1GFN2 Resin
| Step | Process |
|---|---|
| Processing Method | Injection molding |
| Drying Temperature | 105 – 110°C |
| Drying Time | 3 – 4 hours |
| Maximum Moisture Content | < 0.02% |
| Melt Temperature | 300 – 325°C |
| Mold Temperature | 80 – 110°C |
| Storage | Store in original, sealed packaging in a cool, dry place away from direct sunlight |
Critical Processing Warnings:
Injection Molding: This grade is specifically designed for injection molding.
Drying: Proper drying is critical to prevent hydrolysis and achieve optimal mechanical properties.
Glass Reinforcement: This grade contains 20% glass fiber, which may require processing adjustments for optimal surface finish and fiber orientation.
UL Compliance: This grade carries UL94 5VA (2mm), V-1 (1.5mm), and V-0 (6mm) ratings. Ensure processing conditions maintain compliance.
UL746C F1 Rating: This grade is UL746C F1 rated for outdoor suitability.
PFAS-Free: This product does not contain PFAS intentionally added (AMR and EUR sourced only).
Regional Availability: This grade is available in the Americas and Asia Pacific regions.
Storage: Store in original, sealed packaging in a cool, dry place away from direct sunlight.
Related Products for NORYL SE1GFN2 Resin
Explore Engineering Plastics – Browse all engineering plastic materials
About Our Company – Learn more about our supply capabilities and quality assurance
Technical Documents for NORYL SE1GFN2 Resin
| Document Type | Description & Source |
|---|---|
| Manufacturer Official TDS | Complete physical, thermal, and mechanical properties of NORYL SE1GFN2 |
| Manufacturer Official SDS | GHS-compliant safety documentation |
| COA (Certificate of Analysis) | Batch-specific quality certification |
| UL Yellow Card | E121562-624509 – UL safety certification |
Request any document above by:
Email: ruiqingchem@gmail.com
Online form: Our contact page
We reply within one working business day. Please clearly state product (NORYL SE1GFN2) and document type you require.
FAQ about NORYL SE1GFN2 Resin
Q1: What is NORYL SE1GFN2?
A: This grade is a 20% glass fiber reinforced blend of PPE and PS from SABIC . It is an injection moldable grade with non-halogenated flame retardancy, UL94 5VA & V-1 ratings, UL746C F1 outdoor suitability, high heat resistance, good dielectric strength, dimensional stability, hydrolytic stability, and very low moisture absorption .
Q2: What is the difference between NORYL SE1GFN1 and NORYL SE1GFN2?
A: NORYL SE1GFN1 contains 10% glass fiber reinforcement, while NORYL SE1GFN2 contains 20% glass fiber reinforcement . SE1GFN2 offers higher stiffness and strength (flexural modulus 5,500 MPa vs ~3,990 MPa) with similar flame retardancy (UL94 V-1) and outdoor suitability (UL746C F1).
Q3: What are the key features of this grade?
A: 20% glass reinforcement, halogen-free flame retardancy (UL94 5VA at 2mm & V-1 at 1.5mm), UL746C F1 outdoor rating, RTI of 110°C, high stiffness (flexural modulus 5,500–5,600 MPa), high strength (tensile strength 106–120 MPa), good impact resistance (100 J/m notched Izod), low warpage, low shrinkage, very low moisture absorption (0.06%), PFAS-free, and RoHS compliant .
Q4: What are the typical applications for this grade?
A: Solar frames, UPS inverter/charger, indoor and outdoor electrical enclosures, housings, connectors, wall plates, sockets, switches, automotive EV components, energy management applications, and drone components .
Q5: What are the flame ratings of this grade?
A: UL94 5VA at 2mm, V-1 at 1.5mm, and V-0 at 6mm .
Q6: Is this grade suitable for outdoor use?
A: Yes, this grade carries a UL746C outdoor suitability rating of F1 .
Q7: Is this grade halogen-free and PFAS-free?
A: Yes. It contains non-brominated, non-chlorinated flame retardant and does not contain PFAS intentionally added (AMR and EUR sourced only) .
Q8: What is the recommended processing method for this grade?
A: Injection molding. Dry at 105–110°C for 3–4 hours (moisture < 0.02%). Melt temperature: 300–325°C. Mold temperature: 80–110°C .
Q9: What is the UL Yellow Card number for this grade?
A: E121562-624509 .
Q10: What regions is this grade available in?
A: Americas and Asia Pacific .
CTA (Call to Action)
Ready to order NORYL SE1GFN2?
To get a precise quotation and professional technical support, please share:
-
Required quantity (kg)
-
Destination port or delivery address
-
Target application (solar frames, UPS, electrical enclosures, connectors, etc.)
-
Color requirement
-
Document requirement (TDS, SDS, COA, UL docs, etc.)
Sample Policy:
-
Samples are for laboratory validation tests only, not for production use.
-
Buyer bears international sample-shipping freight.
-
If bulk-product performance deviates from sample reference, manufacturer official TDS serves as the authoritative benchmark.
Take action now:
-
📧 Email Us – ruiqingchem@gmail.com
-
📝 Send Inquiry – Use our quick inquiry form
-
💬 Live Chat – Click the bottom-right chat widget to speak directly with our team
After-Sales Support
| Service | Details |
|---|---|
| Quality Inspection Period | All quality-related claims must be submitted within 7 working days after delivery, supported by test data and photographic evidence. |
| Return / Exchange Policy | Confirmed product defects caused by our side trigger replacement or refund. Terms and conditions apply. |
| Logistics Damage | Report shipping damage directly to carrier immediately upon goods receipt. We assist with claim-document preparation. |
| Technical Support | Remote technical guidance available. On-site troubleshooting can be arranged upon special request. |
| Export Documentation | We supply commercial invoice, packing list, bill of lading, COA, and additional compliance certificates on request. |
Disclaimer
DISCLAIMER: All technical data is referenced from original manufacturer typical values for NORYL SE1GFN2. Our company acts as authorized distributor/trader rather than original manufacturer. Final performance depends on processing conditions and part design. Buyers shall independently validate product suitability for individual applications. Our firm bears no liability for product failure caused by improper processing or improper usage. Always reference the latest manufacturer official TDS of NORYL SE1GFN2 as the definitive specification.