描述
Micromax 00L1B High Power Low Thickness Resistor Paste
Type: Chip Resistor Paste
Pack: 100G / 1000G
Viscosity: 80-180 Pa.s
Film Thickness: 18-22 μm
Firing: 850°C / 30 min
Shelf Life: 6 months
Micromax 00L1B delivers high power at low thickness with excellent blendability and improved green strength — engineered for chip resistor applications with 850°C fast firing.
Micromax 00L1B is a high power low thickness resistor paste specifically developed for chip resistor applications requiring efficient power handling at reduced film thickness. This grade delivers high power performance even at low thickness, enabling material-efficient resistor designs. The material offers excellent blendability for low resistivity applications and improved green strength for enhanced handling during printing and assembly processes.
This resistor paste is optimized for screen printing and supports co-firing with high silver terminations at 850°C peak temperature. The cadmium-free, nickel-free and phthalate-free formulation meets international environmental standards. Standard packaging options are 100G and 1000G.
Genuine Micromax Imported Stock and Technical Support
We maintain stable inventory of authentic Micromax 00L1B high power low thickness resistor paste. Factory-original TDS and batch-specific COA can be provided upon request.
Request Sample, TDS & Quotation
Complete TDS, COA, and regulatory documentation available
Core Advantages of Micromax 00L1B
- High power at low thickness — efficient power handling with reduced material consumption
- Excellent blendability — broad resistance tuning for low resistivity applications
- Improved green strength — robust handling during screen printing and assembly
- Fast firing profile — 850°C peak with 30-minute total cycle for high throughput
- High silver termination compatible — validated for Ag/Pd termination systems
- RoHS, REACH compliant; Cadmium/Nickel/Phthalate free — satisfies global environmental regulations
Main Applications
- Chip Resistors — low resistivity chip resistor production
- Low Resistivity Applications — ultra-low resistance chip resistor designs
- High Power Low Thickness Designs — power-efficient resistor components
- Surface Mount Devices — SMD resistor components for consumer and industrial electronics
Full Technical Parameters
| Property | Typical Value | Test / Reference |
| Product Type | Thick film chip resistor paste | — |
| Application | Chip resistor manufacturing | — |
| Packaging Specification | 100G, 1000G | Standard packing |
| Viscosity (Brookfield HBT 10 rpm) | 80-180 Pa.s | SC4-14/6R, 25°C |
| Recommended Film Thickness | 18-22 μm | Dried thickness |
| Drying Temperature | 150°C | 10 minutes |
| Firing Peak Temperature | 850°C | 10 min at peak, 30 min total |
| High Power Low Thickness | Designed for high power at low thickness | — |
| Blendability | Excellent for low resistivity applications | — |
| Green Strength | Improved | — |
| Termination Compatibility | High silver terminations (Micromax 5426 Ag/Pd) | — |
| Substrate Compatibility | 96% alumina | — |
| Environmental Compliance | RoHS, REACH, Cadmium free, Nickel free, Phthalate free | — |
| Shelf Life | 6 months in unopened containers | — |
| Storage Temperature | 5-30°C | — |
Note: All listed values are typical and may vary by batch. Independent qualification testing is required prior to production use.
Recommended Processing Conditions
| Parameter | Recommended Value |
| Mixing Prior to Use | Slow gentle hand-stirring, 1-2 minutes |
| Optimal Printing Temperature | 20-23°C |
| Leveling | Allow to level at room temperature |
| Drying Temperature | 150°C |
| Drying Time | 10 minutes |
| Dried Film Thickness | 18-22 μm |
| Firing Peak Temperature | 850°C |
| Total Firing Cycle | 30 minutes (10 min at peak) |
| Substrate | 96% alumina |
Handling and Storage Recommendations
| Storage Rules | Store in tightly sealed containers in clean, stable environment at 5-30°C. |
| Shelf Life | 6 months in unopened containers from date of shipment. |
| Pre-use Preparation | Thoroughly mix prior to use. Some settling may occur. |
| Thinning | Not normally required; use Micromax 8250(T) thinner sparingly for evaporative losses. |
Official Technical Documentation
| Document Type | Document Introduction | Document Request |
| TDS | Micromax 00L1B original factory technical data sheet | Request TDS |
| COA | Batch-specific certificate of analysis | Request COA |
| SDS | Safety Data Sheet for handling and storage | Request SDS |
Frequently Asked Questions
What is Micromax 00L1B?
Micromax 00L1B is a high power low thickness resistor paste designed for chip resistor applications. It delivers high power at low film thickness with excellent blendability for low resistivity designs.
What is the viscosity of Micromax 00L1B?
Micromax 00L1B exhibits a viscosity between 80 and 180 Pa.s when measured with Brookfield HBT at 10 rpm, SC4-14/6R spindle, 25°C.
What is the recommended processing profile for Micromax 00L1B?
Recommended processing: dry at 150°C for 10 minutes, then fire at 850°C peak for 10 minutes within a 30-minute total cycle.
What is the recommended film thickness for Micromax 00L1B?
Micromax 00L1B is optimized for 18-22 μm dried film thickness.
What terminations are compatible with Micromax 00L1B?
Micromax 00L1B is compatible with high silver terminations, with reported properties obtained using Micromax 5426 Ag/Pd termination.
Is Micromax 00L1B environmentally compliant?
Yes. Micromax 00L1B contains no intentionally added cadmium, nickel or phthalates, meeting RoHS and REACH environmental standards.
What packaging sizes are available for Micromax 00L1B?
Micromax 00L1B is supplied in 100G and 1000G containers. For larger volume requirements, please contact our sales team.
Get Micromax 00L1B Bulk Pricing and Technical Support
We supply genuine Micromax 00L1B high power low thickness resistor paste for electronic component manufacturing. Contact us for bulk pricing, sample availability, technical documents, and application support.
Inquire Bulk Price & Technical Support
Disclaimer: All technical data on this page are for general guidance only and are not product specifications. Buyers must carry out independent trials and verify suitability before bulk ordering. Actual values may vary between production lots.