描述
Micromax 0001L Low Ohm Chip Resistor Paste
Type: Chip Resistor Paste
Pack: 100G / 1000G
Viscosity: 150-240 Pa.s
Resistivity: 1 Ω/sq
Firing: 850°C / 30 min
Shelf Life: 6 months
Micromax 0001L delivers 1 Ω/sq low ohm performance with balanced cost vs TCR and tight resistance distribution — engineered for high productivity chip resistor manufacturing with excellent printability and firing profile insensitivity.
Micromax 0001L is a low ohm thick film paste designed for chip resistor production where cost efficiency and consistent TCR performance are equally critical. Formulated to deliver 1 Ω/sq resistivity with tight resistance distribution, this grade supports high manufacturing yields while maintaining stable electrical properties across production batches. The material exhibits linear blend behavior, enabling resistance tuning with adjacent members including 0020L and 00L1L.
This resistor paste offers excellent printability and is insensitive to firing profile variations and chip size changes, ensuring reliable performance across different manufacturing conditions. It is optimized for 14-16 μm dried film thickness using 250-325 mesh screens with 10-15 μm emulsion. The formulation is cadmium-free, nickel-free and phthalate-free, meeting global environmental standards. Standard packaging options are 100G and 1000G to accommodate varying production scales.
Genuine Micromax Imported Stock and Technical Support
We maintain stable inventory of authentic Micromax 0001L low ohm chip resistor paste. Factory-original TDS and batch-specific COA can be provided upon request for electronic component manufacturing projects.
Request Sample, TDS & Quotation
Complete TDS, COA, and regulatory documentation available
Core Advantages of Micromax 0001L
- Low ohm formulation — fixed 1 Ω/sq resistivity for precise low-resistance chip resistor applications
- Balanced cost vs TCR performance — optimal trade-off between manufacturing cost and temperature stability
- Tight resistance distribution — consistent electrical properties across production runs
- High productivity and yields — designed for high-volume manufacturing efficiency
- Insensitive to firing profile — reliable performance across varied firing conditions
- Insensitive to chip size — consistent resistance values across different chip geometries
- Linear blend behavior — adjustable resistance range by blending with adjacent grades
- Excellent printability — optimized for 250-325 mesh screens at 14-16 μm dried thickness
- RoHS, REACH compliant; Cadmium/Nickel/Phthalate free — satisfies global environmental regulations
Main Applications
- Chip Resistors — low ohm chip resistor mass production
- Current Sensing Resistors — low resistance current detection applications
- Hybrid Circuits — resistor networks in hybrid microcircuits
- Surface Mount Devices — SMD resistor components for consumer and industrial electronics
Full Technical Parameters
| Property | Typical Value | Test / Reference |
| Product Type | Thick film chip resistor paste | — |
| Application | Chip resistor manufacturing | — |
| Packaging Specification | 100G, 1000G | Standard packing |
| Resistivity | 1 Ω/sq | 8 sq geometry |
| Viscosity (Brookfield HAT 10 rpm) | 150-240 Pa.s | SC4-14/6R, 25°C |
| Recommended Mesh | 250-325 mesh | — |
| Emulsion Thickness | 10-15 μm | — |
| Dried Film Thickness | 14-16 μm | Recommended range |
| Leveling Time | 5-10 min | Room temperature |
| Drying Temperature | 150°C | 10-15 minutes |
| Firing Peak Temperature | 850°C | 10 min at peak, 30 min total |
| Short Time Overload | ≤ ±0.1% ΔR | 2.5× rated power, 400V max |
| ESD Performance | HBM 150pF / 10000Ω | 1.0mm × 1.0mm, untrimmed |
| Termination Compatibility | Micromax 5426, 5421E, 5418 Ag/Pd, 5463 Ag | — |
| Substrate Compatibility | 96% alumina | — |
| Blendability | Linear blend behavior with 0020L, 00L1L | — |
| Environmental Compliance | RoHS, REACH, Cadmium free, Nickel free, Phthalate free | — |
| Shelf Life | 6 months in unopened containers | — |
| Storage Temperature | 5-30°C | — |
Note: All listed values are typical and may vary by batch. Independent qualification testing is required prior to production use.
Recommended Processing Conditions
| Parameter | Recommended Value |
| Screen Mesh | 250-325 mesh |
| Emulsion Thickness | 10-15 μm |
| Dried Film Thickness | 14-16 μm |
| Leveling Time | 5-10 minutes |
| Drying Temperature | 150°C |
| Drying Time | 10-15 minutes |
| Firing Peak Temperature | 850°C |
| Total Firing Cycle | 30 minutes (10 min at peak) |
| Substrate | 96% alumina |
Handling and Storage Recommendations
| Storage Rules | Store in tightly sealed containers in clean, stable environment at 5-30°C. |
| Shelf Life | 6 months in unopened containers from date of shipment. |
| Pre-use Preparation | Thoroughly mix prior to use. Some settling may occur. |
| Thinning | Not normally required; use Micromax 8250(T) thinner sparingly for evaporative losses. |
Official Technical Documentation
| Document Type | Document Introduction | Document Request |
| TDS | Micromax 0001L original factory technical data sheet | Request TDS |
| COA | Batch-specific certificate of analysis | Request COA |
| SDS | Safety Data Sheet for handling and storage | Request SDS |
Frequently Asked Questions
What is Micromax 0001L?
Micromax 0001L is a low ohm thick film paste that delivers 1 Ω/sq resistivity for chip resistor production. It balances cost against TCR performance while maintaining tight resistance distribution and high manufacturing yields.
What is the resistivity of Micromax 0001L?
Micromax 0001L provides a fixed resistivity of 1 Ω/sq, measured using 8 square resistor geometry on 96% alumina substrates.
What is the viscosity of Micromax 0001L?
This paste exhibits viscosity in the range of 150-240 Pa.s when measured with Brookfield HAT at 10 rpm, SC4-14/6R spindle, 25°C.
What is the recommended processing profile for Micromax 0001L?
Recommended processing: level for 5-10 minutes, dry at 150°C for 10-15 minutes, then fire at 850°C peak for 10 minutes within a 30-minute total cycle.
What is the recommended dried film thickness for Micromax 0001L?
Micromax 0001L is optimized for 14-16 μm dried film thickness using 250-325 mesh screens with 10-15 μm emulsion.
Is Micromax 0001L environmentally compliant?
Yes. Micromax 0001L contains no intentionally added cadmium, nickel or phthalates, meeting RoHS and REACH environmental standards.
What terminations are compatible with Micromax 0001L?
Micromax 0001L is compatible with high silver terminations including Micromax 5426, 5421E, 5418 Ag/Pd, and 5463 Ag termination pastes.
What packaging sizes are available for Micromax 0001L?
Micromax 0001L is supplied in 100G and 1000G containers. For larger volume requirements, please contact our sales team.
Get Micromax 0001L Bulk Pricing and Technical Support
We supply genuine Micromax 0001L low ohm chip resistor paste for electronic component manufacturing. Contact us for bulk pricing, sample availability, technical documents, and application support.