描述
Micromax 0001B Low Resistivity Chip Resistor Paste
Type: Chip Resistor Paste
Pack: 100G / 1000G
Viscosity: 80-180 Pa.s
Resistivity: 0.85-1.15 Ω/sq
Firing: 850°C / 30 min
Shelf Life: 6 months
Micromax 0001B delivers low resistivity (0.85-1.15 Ω/sq) with high power performance at low thickness — engineered for low-cost, high productivity chip resistor manufacturing with excellent blendability.
Micromax 0001B is a low resistivity thick film paste engineered specifically for chip resistor mass production where cost efficiency and consistent output are paramount. Formulated to deliver reliable power handling even at reduced film thickness, this grade supports miniaturized resistor designs without compromising electrical performance. The material features excellent blendability for low resistivity applications, enabling manufacturers to fine-tune resistance values across a broad range while maintaining stable TCR characteristics.
This resistor paste offers improved green strength for enhanced handling during printing and assembly processes. It is optimized for high-speed screen printing and supports co-firing with high silver termination materials at a peak temperature of 850°C. The cadmium-free, nickel-free and phthalate-free formulation meets international environmental standards including RoHS and REACH. Standard packaging options are 100G and 1000G to accommodate varying production scales.
Genuine Micromax Imported Stock and Technical Support
We maintain stable inventory of authentic Micromax 0001B low resistivity chip resistor paste. Factory-original TDS and batch-specific COA can be provided upon request for electronic component manufacturing projects.
Request Sample, TDS & Quotation
Complete TDS, COA, and regulatory documentation available
Core Advantages of Micromax 0001B
- Low resistivity formulation — 0.85-1.15 Ω/sq for precise low-resistance chip resistor applications
- High power at low thickness — reliable power handling with reduced material consumption
- Excellent blendability — broad resistance tuning without sacrificing electrical performance
- Improved green strength — robust handling during screen printing and assembly stages
- Fast firing profile — 850°C peak with 30-minute total cycle for high manufacturing throughput
- Well controlled TCR — -200 to 200 ppm/°C across hot and cold temperature ranges
- High silver termination compatible — validated for Ag/Pd termination systems
- RoHS, REACH compliant; Cadmium/Nickel/Phthalate free — satisfies global environmental regulations
Main Applications
- Chip Resistors — low resistivity chip resistor mass production
- Hybrid Circuits — resistor networks in hybrid microcircuits requiring low resistance values
- Surface Mount Devices — SMD resistor components for consumer and industrial electronics
- Automotive Electronics — resistor components requiring high power handling and thermal stability
Full Technical Parameters
| Property | Typical Value | Test / Reference |
| Product Type | Thick film chip resistor paste | — |
| Application | Chip resistor manufacturing | — |
| Packaging Specification | 100G, 1000G | Standard packing |
| Viscosity (Brookfield HBT 10 rpm) | 80-180 Pa.s | SC4-14/6R, 25°C |
| Resistivity (25°C, 20μm dried) | 0.85-1.15 Ω/sq | 500 sq geometry |
| Dried Film Thickness | 18-22 μm | Recommended range |
| Drying Temperature | 150°C | 10 minutes |
| Firing Peak Temperature | 850°C | 10 min at peak, 30 min total |
| Hot TCR (25-125°C) | -200 to 200 ppm/°C | 500 sq geometry |
| Cold TCR (-55-25°C) | -200 to 200 ppm/°C | 500 sq geometry |
| Termination Compatibility | High silver terminations (Micromax 5426 Ag/Pd) | — |
| Substrate Compatibility | 96% alumina substrates | — |
| Blendability | Excellent for low resistivity applications | — |
| Green Strength | Improved | — |
| Environmental Compliance | RoHS, REACH, Cadmium free, Nickel free, Phthalate free | — |
| Shelf Life | 6 months in unopened containers | — |
| Storage Temperature | 5-30°C | — |
Note: All listed values are typical and may vary by batch. Independent qualification testing is required prior to production use.
Recommended Processing Conditions
| Parameter | Recommended Value |
| Mixing Prior to Use | Slow gentle hand-stirring, 1-2 minutes |
| Optimal Printing Temperature | 20-23°C |
| Drying Temperature | 150°C |
| Drying Time | 10 minutes |
| Dried Film Thickness | 18-22 μm |
| Firing Peak Temperature | 850°C |
| Total Firing Cycle | 30 minutes (10 min at peak) |
| Substrate | 96% alumina |
Handling and Storage Recommendations
| Storage Rules | Store in tightly sealed containers in clean, stable environment at 5-30°C. |
| Shelf Life | 6 months in unopened containers from date of shipment. |
| Pre-use Preparation | Thoroughly mix prior to use — slow gentle hand-stirring for 1-2 minutes. |
| Thinning | Not normally required; use Micromax 8250(T) thinner only for minor adjustments. |
| Operation Protection | Print in clean, well-ventilated area. Avoid metal contamination and dust. |
Official Technical Documentation
| Document Type | Document Introduction | Document Request |
| TDS | Micromax 0001B original factory technical data sheet | Request TDS |
| COA | Batch-specific certificate of analysis | Request COA |
| SDS | Safety Data Sheet for handling and storage | Request SDS |
Frequently Asked Questions
What is Micromax 0001B?
Micromax 0001B is a low ohm thick film paste formulated for chip resistor production requiring low resistance values. It combines high power output with thin-film efficiency, good mixability across resistivity ranges, and enhanced wet-state durability during printing.
What is the resistivity of Micromax 0001B?
The resistivity range for Micromax 0001B is 0.85-1.15 Ω/sq, measured at 25°C using 20 μm dried film thickness and 500 square resistor geometry.
What is the viscosity of Micromax 0001B?
Micromax 0001B exhibits a viscosity between 80 and 180 Pa.s when tested with Brookfield HBT at 10 rpm, SC4-14/6R spindle, 25°C.
What is the recommended drying and firing profile for Micromax 0001B?
Recommended processing includes drying at 150°C for 10 minutes, followed by a 30-minute firing cycle with peak temperature of 850°C maintained for 10 minutes.
Is Micromax 0001B environmentally compliant?
Yes, Micromax 0001B contains no intentionally added cadmium, nickel or phthalates, meeting RoHS and REACH environmental requirements for global markets.
What terminations are compatible with Micromax 0001B?
This paste is engineered for use with high silver-content terminations. Performance data was established using Micromax 5426 Ag/Pd termination paste.
What packaging sizes are available for Micromax 0001B?
Micromax 0001B is supplied in 100G and 1000G containers. For larger volume requirements, please contact our sales team to discuss supply arrangements.
How should Micromax 0001B be stored?
Store in original sealed containers at 5-30°C in a clean, dry environment. Unopened containers maintain a 6-month shelf life from the shipment date. Stir gently before use.
Get Micromax 0001B Bulk Pricing and Technical Support
We supply genuine Micromax 0001B low resistivity chip resistor paste for electronic component manufacturing. Contact us for bulk pricing, sample availability, technical documents, and application support.
Inquire Bulk Price & Technical Support
Disclaimer: All technical data on this page are for general guidance only and are not product specifications. Buyers must carry out independent trials and verify suitability before bulk ordering. Actual values may vary between production lots.