532G-13054 Ruby Red is a 532G-13054 Ruby Red PFA Powder Topcoat from Chemours‘ Teflon industrial coatings portfolio, genuinely manufactured by Chemours and imported as original product. As an authorized distributor and trader, we supply genuine material with full traceability and direct access to official Chemours technical documentation. For more product options and company information, please visit our website at https://szrqchem.com/.
This 532G-13054 Ruby Red PFA Powder Topcoat is a filled version of PFA (perfluoroalkoxy) powder coating, specifically formulated to reduce permeation. PFA is a melt‑processable fluoropolymer that melts and flows during baking to form nonporous, smooth, and highly durable films. These multi‑coat systems provide higher continuous use temperatures (260°C / 500°F), have a high dielectric strength, and are considered tougher than PTFE or FEP.
532G-13054 Ruby Red should be considered whenever permeation is thought to be a considerable risk to the performance of normal fluoropolymer coatings. This filled coating can be applied over a broad range of thicknesses; a coating thickness of 200 – 500 μm (8 – 20 mil) is recommended. With a maximum total film build of up to 40 mils (approx. 1,016 μm), 532G-13054 offers exceptional thick film protection for demanding industrial applications.
The coating is available in a ruby red pigmented finish, providing a distinctive industrial appearance while offering superior protection. As a powder coating, 532G-13054 contains zero VOCs, offering significant environmental and worker safety advantages over solvent‑based alternatives.
532G-13054 is widely used in heat exchangers, tanks, valves, vessels, chemical processing equipment, automatic welding equipment, molds, carburetor shafts, linkage devices, cruise control parts, filters, cryogenic applications, and aerospace components. With regular stock availability, we support both trial orders and large‑volume bulk shipments for chemical processing, semiconductor equipment, aerospace, and other demanding industrial applications.
Key Features of 532G-13054 Ruby Red PFA Powder Topcoat
-
Filled / Reinforced Formulation – Specifically formulated to reduce permeation, providing superior barrier protection compared to standard PFA grades.
-
Exceptional Permeation Resistance – Offers outstanding resistance to chemical permeation; should be considered whenever permeation poses a risk to fluoropolymer coating performance.
-
High Build / Thick Film Capability – Supports maximum total film build up to 40 mils (approx. 1,016 μm) with recommended DFT of 200 – 500 μm (8 – 20 mil).
-
Ruby Red Finish – Distinctive ruby red pigmented finish for easy visual identification and consistent industrial appearance.
-
High Temperature Resistance – Continuous service up to 260°C (500°F) with intermittent service up to 316°C (600°F).
-
Excellent Non‑Stick Release – PFA‑based formulation provides outstanding release properties; surface energy is extremely low at 18‑20 dynes/cm.
-
Ultra‑Low Coefficient of Friction – Friction coefficient stabilizes between 0.05‑0.20, with static friction reduced by over 70% compared to bare metal.
-
Superior Chemical Resistance – Resists most acids, bases, and solvents; can tolerate 98% sulfuric acid and 30% sodium hydroxide.
-
Exceptional Weatherability – Outdoor exposure 10+ years with >80% gloss retention.
-
Nonporous Film Formation – Melts and flows during baking to form nonporous, pinhole‑free films providing excellent barrier protection.
-
Zero VOC Formulation – Powder coating contains 0 g/kg VOC, offering significant environmental and worker safety advantages.
-
Broad Substrate Compatibility – Can be applied to carbon steel, aluminum, stainless steel, alloy steel, brass, magnesium, as well as non‑metallic materials including glass, fiberglass, and certain rubbers and plastics.
-
Tougher than PTFE or FEP – PFA offers superior toughness and durability compared to PTFE or FEP.
Typical Applications for 532G-13054 Ruby Red
| Industry | Typical Components & Considerations |
|---|---|
| Chemical Processing | Tanks, vessels, reactors, heat exchange linings, piping, gas scrubbers – requires permeation resistance and chemical barrier protection |
| Heat Exchangers | Heat exchanger surfaces – requires nonstick, corrosion protection, and permeation resistance |
| Storage Tanks | Tank linings – thick film build provides exceptional barrier protection against chemical permeation |
| Automatic Welding Equipment | Welding fixtures and tooling – spatter resistance and easy cleaning |
| Mold & Tooling | Injection molds, rubber molds, plastic molds – release properties and extended mold life |
| Automotive | Carburetor shafts, linkage devices, cruise control parts – dry lubrication and corrosion resistance |
| Aerospace | Aerospace fasteners, cryogenic components – wide temperature range from cryogenic to high temperature |
| Filtration Systems | Coated filter elements – reduced fouling and improved flow |
| Semiconductor Equipment | High‑purity components – requires high dielectric strength and chemical resistance |
| Commercial Laundry | Dryer baskets – nonstick and corrosion resistance |
| General Industrial | Components requiring PFA nonstick properties with ruby red finish and permeation resistance |
Material Advantages
The 532G-13054 Ruby Red PFA Powder Topcoat is a high‑performance PFA powder coating that delivers:
-
Exceptional Permeation Resistance – The filled formulation provides outstanding protection against chemical permeation, making it ideal for storage tanks, chemical processing equipment, and other applications requiring barrier protection.
-
Superior Thermal Stability – Maintains performance at continuous service temperatures up to 260°C (500°F), with intermittent service up to 316°C (600°F).
-
High Build Capability – Supports total film thickness up to 40 mils (approx. 1,016 μm), providing enhanced abrasion resistance, corrosion protection, and extended service life.
-
Exceptional Nonstick Performance – Provides outstanding release properties; coating surface energy is only 18‑20 dynes/cm, with material adhesion less than 10% compared to uncoated surfaces.
-
Ultra‑Low Friction – Friction coefficient stabilizes between 0.05‑0.20, with static friction reduced by over 70% compared to bare metal.
-
Chemical Inertness – Resistant to most acids, bases, and solvents; can tolerate 98% sulfuric acid and 30% sodium hydroxide.
-
Excellent Weatherability – Outdoor exposure 10+ years with >80% gloss retention.
-
Zero VOC – Powder formulation contains no VOCs, offering significant environmental and worker safety advantages.
-
Tougher than PTFE or FEP – PFA offers superior toughness and durability compared to PTFE or FEP.
-
Wide Temperature Range – Applicable across extreme temperature ranges from -270°C cryogenic to 260°C high temperature.
-
Broad Substrate Compatibility – Applicable to carbon steel, aluminum, stainless steel, alloy steel, brass, magnesium, as well as non‑metallic materials including glass, fiberglass, and certain rubbers and plastics.
-
No Clear Topcoat Required – Unlike some other PFA systems, 532G-13054 does not require a clear topcoat as the final layer.
Chemours, as the inventor of Teflon, brings over 80 years of fluoro‑polymer expertise, ensuring batch‑to‑batch consistency, reliable supply, and full technical support.
Typical Properties
| Property | 532G-13054 Ruby Red | Unit / Remarks |
|---|---|---|
| Product Type | PFA Powder Topcoat – Filled, High Build | – |
| Color | Ruby Red | – |
| Form | Powder | – |
| FDA Compliance | No – Not FDA compliant per 21CFR | – |
| Coverage | 18.4 m²/kg (87.8 ft²/lb) | At 1.0 mil DFT |
| Average Particle Size | 61 – 101 μm | – |
| Bulk Density | 75 – 109 g/100 cc | – |
| Max Continuous Use Temp. | 260°C (500°F) | – |
| Intermittent Use Temp. | 316°C (600°F) | – |
| Recommended Total DFT | 200 – 500 μm (8 – 20 mil) | – |
| Max Total Film Build | Up to 40 mil (approx. 1,016 μm) | – |
| First Coat DFT | 70-80 μm (2.8-3.1 mil) | – |
| Subsequent Coat DFT | Up to 150 μm (5.9 mil) per coat | – |
| Application Method | Electrostatic Spray / Fluidized Bed | – |
| Recommended Primer | 420G-703 | – |
| CAS Number | 26655-00-5 | – |
| Shelf Life | Indefinite | 18-27°C / 65-80°F |
Important Notes on Typical Data:
-
Values listed are typical and sourced from Chemours official data sheets. They do not constitute binding product specification.
-
Physical constants are averages only and may vary up to ±5% of the values shown.
-
Final performance depends on substrate preparation, application method, and curing conditions.
-
Chemours original TDS shall serve as definitive technical reference. Request the latest official TDS from our sales team.
Processing Guidelines
| Step | Process |
|---|---|
| Substrate | Aluminum, stainless steel, carbon steel – acceptable substrates with proper primer |
| Surface Preparation | Thoroughly clean and roughen substrate. Grit blast profile: Ra of 2.5–3 μm (100–125 μm) maximum |
| Screening | Through 60 mesh (approx. 250 μm) screen |
| Primer Application | Recommended primer: 420G-703. Filter primer through 40-mesh (approx. 400 μm) |
| First Coat Application | Apply powder onto wet primer and cold substrate using spray voltage of 15–30 kV. Part must be well grounded |
| First Coat DFT | 70-80 μm (2.8-3.1 mil) |
| First Coat Bake | 10–20 min at 232–260°C (450–500°F), then 10–20 min at 385–393°C (725–740°F) |
| Subsequent Coats | Apply powder to cold part or hot flock. DFT up to 150 μm (5.9 mil) per coat |
| Subsequent Coats Bake | 360–377°C (680–710°F) for 20 min |
| Final Coat Bake | 2–4 hours at 340–365°C (645–660°F) for optimum flow out |
| Storage | Store at normal room temperature 18–27°C (65–80°F). Seal package to avoid humidity or contamination |
| Shelf Life | Indefinite when properly stored |
Critical Processing Warnings:
-
Primer Required: 532G-13054 is a topcoat and must be used with a compatible primer system (e.g., 420G-703). Unless explicitly noted, most Teflon industrial coatings require primer application.
-
First Coat Limitation: First coat is limited to 70-80 μm (2.8-3.1 mil); subsequent coats can be applied up to 150 μm (5.9 mil) per coat.
-
No Clear Topcoat Required: Unlike some other PFA systems, 532G-13054 does not require a clear topcoat as the final layer.
-
Surface Preparation: Proper surface preparation is critical for adhesion. Ensure surfaces are clean, dry, and properly roughened.
-
Temperature Control: Keep the difference between metal and oven temperature small to prevent bubbling. Bake temperature of the first coat is important for adhesion to the primer.
-
Shelf Life: Powders may form lumps under prolonged storage; sieving through a coarse screen will restore the powder.
-
Storage: Store in original, sealed containers in a cool, dry place away from direct sunlight at 18-27°C (65-80°F).
Related Products
-
Explore Teflon PTFE Coatings – Browse all Teflon industrial coating options
-
850G-300 Clear – Teflon PTFE Acid Primer – Acid primer for PTFE, PFA, and FEP topcoat systems
-
953G-506 Dark Violet – FEP Waterborne Primer – FEP primer for multi-coat food contact systems
-
About Our Company – Learn more about our supply capabilities and quality assurance
External Reference
For authoritative information, please refer to the following official resources:
-
Chemours Official Website – Corporate headquarters and product portfolio overview
-
Teflon Industrial Coatings Product Center – Official technical literature and application guides
Technical Documents
| Document Type | Description & Source |
|---|---|
| Chemours Official TDS | Complete physical, thermal, and mechanical properties of 532G-13054 Ruby Red, issued by Chemours original |
| Chemours Official SDS | GHS‑compliant chemical safety documentation, original Chemours document |
| Chemours Distributor Authorization Certificate | Proof of our authorized‑distributor qualification for Chemours Teflon series, available upon request |
| COA (Certificate of Analysis) | Batch‑specific quality certification |
| Application & Usage Guide | Detailed application guidance for PFA powder coating systems |
Request any document above by:
-
Email:
ruiqingchem@gmail.com -
Online form: Our contact page
We reply within one working business day. Please clearly state product (532G-13054 Ruby Red) and document type you require.
FAQ
Q1: What is 532G-13054 Ruby Red and what is it used for?
A: 532G-13054 Ruby Red is a filled, high build PFA powder topcoat from the Teflon industrial coatings portfolio. It is specifically formulated to reduce permeation and should be considered whenever permeation poses a risk to fluoropolymer coating performance. It is widely used in chemical processing equipment, heat exchangers, tanks, vessels, automatic welding equipment, molds, automotive components, and aerospace applications.
Q2: Is 532G-13054 Ruby Red FDA compliant?
A: No. 532G-13054 is not FDA compliant for food contact applications per 21CFR. It is suitable for industrial and chemical processing applications.
Q3: What is the difference between 532G-13054 and 532G-13051?
A: Both are Ruby Red PFA powders. 532G-13054 has a larger average particle size (61-101 μm) compared to 532G-13051 (24-32 μm), making 532G-13054 more suitable for thick film / high build applications. Both offer exceptional permeation resistance.
Q4: What is the recommended film build of 532G-13054 Ruby Red?
A: Recommended DFT is 200 – 500 μm (8 – 20 mil). First coat is limited to 70-80 μm (2.8-3.1 mil), with subsequent coats up to 150 μm (5.9 mil) per coat. Maximum total film build is up to 40 mils (approx. 1,016 μm).
Q5: What primer is recommended for 532G-13054 Ruby Red?
A: The recommended primer is 420G-703. Unless explicitly noted, most Teflon industrial coatings require primer application.
Q6: Is a clear topcoat required for 532G-13054 Ruby Red?
A: No. Unlike some other PFA systems, 532G-13054 does not require a clear topcoat as the final layer.
Q7: What is the temperature range of 532G-13054 Ruby Red?
A: Continuous service up to 260°C (500°F) with intermittent service up to 316°C (600°F). The coating system is also suitable for cryogenic applications down to -270°C.
Q8: What is the cure temperature for 532G-13054 Ruby Red?
A: First coat bake: 10–20 min at 232–260°C, then 10–20 min at 385–393°C (725–740°F). Subsequent coats: 360–377°C (680–710°F) for 20 min. Final coat: 2–4 hours at 340–365°C (645–660°F) for optimum flow.
Q9: What is the particle size of 532G-13054 Ruby Red?
A: The average particle size is 61 – 101 μm.
Q10: What is the shelf life of 532G-13054 Ruby Red?
A: Powders can be stored indefinitely under optimal storage conditions at 18-27°C (65-80°F). Powders may form lumps under prolonged storage; sieving through a coarse screen will restore the powder.
Q11: What is the lead time for orders?
A: Regular orders ship within 7‑10 working days after payment confirmation. Large‑volume or urgent orders can be negotiated.
CTA (Call to Action)
Ready to order 532G-13054 Ruby Red?
To get a precise quotation and professional technical support, please share:
-
Required quantity (kg)
-
Destination port or delivery address
-
Target application (chemical processing, heat exchangers, tanks, etc.)
-
Required total film thickness (recommended 200-500 μm / 8-20 mil)
-
Primer requirement (420G-703 recommended)
-
Document requirement (TDS, SDS, COA, etc.)
Sample Policy:
-
Samples are for laboratory validation tests only, not for production use.
-
Buyer bears international sample‑shipping freight.
-
If bulk‑product performance deviates from sample reference, Chemours official TDS serves as the authoritative benchmark.
Take action now:
-
📧 Email Us –
ruiqingchem@gmail.com -
📝 Send Inquiry – Use our quick inquiry form
-
💬 Live Chat – Click the bottom‑right chat widget to speak directly with our team
After‑Sales Support
| Service | Details |
|---|---|
| Quality Inspection Period | All quality‑related claims must be submitted within 7 working‑days after delivery, supported by test data and photographic evidence. |
| Return / Exchange Policy | Confirmed product defects caused by our side trigger replacement or refund. Terms and conditions apply. |
| Logistics Damage | Report shipping damage directly to carrier immediately upon goods receipt. We assist with claim‑document preparation. |
| Technical Support | Remote technical guidance available. On‑site troubleshooting can be arranged upon special request. |
| Export Documentation | We supply commercial invoice, packing list, bill of lading, COA, and additional compliance certificates on request. |
Disclaimer
DISCLAIMER: All technical data is referenced from original Chemours typical values for the 532G-13054 Ruby Red PFA Powder Topcoat. Our company acts as authorized distributor/trader rather than original manufacturer. Final performance depends on substrate preparation, application method, and curing conditions. Buyers shall independently validate product suitability for individual applications. Our firm bears no liability for coating failure caused by improper application or improper usage. Always reference the latest Chemours official TDS of the 532G-13054 Ruby Red PFA Powder Topcoat as the definitive specification.