描述
ExxonMobil Vistamaxx 6902 High Flow Propylene Elastomer for Compounding & Modification
MFR (230°C/2.16kg): 100 g/10min
Hardness: 76 Shore A
✅ High Flow
Vistamaxx 6902 is a high-flow propylene-based elastomer primarily composed of isotactic propylene repeat units with random ethylene distribution, produced using ExxonMobil’s proprietary metallocene catalyst technology. This grade offers exceptional flow characteristics while maintaining elasticity, making it an ideal choice for compounding, polymer modification, and hot melt adhesive applications. RoHS compliant and suitable for industrial applications.
With a high melt flow rate of 100 g/10min (230°C/2.16kg), this grade delivers excellent processability and enhanced flow characteristics, enabling faster production cycles and improved filler dispersion in demanding compounding applications.
The product offers excellent adhesion to conventional and metallocene PP and PE, good chemical resistance to aqueous systems and non-hydrocarbon based fluids, and can be blended with PE, PP, and other polymers including styrenic block copolymers. Its balanced performance makes it a versatile modifier for a wide range of polyolefin systems.
Supplied in free-flowing pellet form, Vistamaxx 6902 is particularly suited for compounding, polymer modification, and hot melt adhesive formulations where high flow, adhesion, and compatibility with polyolefins are critical.
Learn more about the ExxonMobil Vistamaxx product portfolio.
📩 Request Pricing, TDS & Samples
✅ Same-day quotation & technical support available
Vistamaxx 6902 Quick Specs
| Product Name | ExxonMobil Vistamaxx 6902 Propylene Elastomer |
| Grade | Vistamaxx 6902 |
| Brand | ExxonMobil |
| Manufacturer | ExxonMobil Product Solutions |
| Material Type | Propylene-Based Elastomer / Performance Polymer |
| Form | Free-Flowing Pellets |
| Density | 0.869 g/cm³ |
| MFR (190°C/2.16kg) | 43 g/10min |
| MFR (230°C/2.16kg) | 100 g/10min |
| Ethylene Content | 12 wt% |
| Hardness | 76 Shore A |
| Applications | Compounding, polymer modification, hot melt adhesives |
Vistamaxx 6902 Key Features
- High melt flow rate (100 g/10min at 230°C) for exceptional processability and flow.
- Excellent adhesion to conventional and metallocene PP and PE substrates.
- Good chemical resistance to aqueous systems and non-hydrocarbon based fluids.
- Enhanced flow characteristics while maintaining elasticity and performance.
- Can be blended with PE, PP, and other polymers including styrenic block copolymers.
- RoHS compliant for environmentally conscious applications.
- Supplied in free-flowing pellet form for easy handling and processing.
Typical Applications
- Compounding for enhanced flow and filler dispersion
- Polymer modification for improved processability
- Hot melt adhesive formulations requiring high flow and adhesion
- Blending with PE, PP, and styrenic block copolymers
- Adhesive applications requiring good chemical resistance
- Polyolefin modification for enhanced elasticity and processability
This grade is the preferred choice for compounders and formulators requiring high flow, excellent adhesion, and compatibility with a wide range of polymer systems.
Related Products
| ExxonMobil Vistamaxx 3020FL Propylene Elastomer | Film appearance grade for blown film and thermoforming with enhanced melt strength. |
| ExxonMobil Vistamaxx 8580 Propylene Elastomer | Very low viscosity grade for hot melt adhesives and compounding. |
| ExxonMobil Vistamaxx Tough T1600 Propylene Elastomer | High melt strength grade for film extrusion and impact modification. |
Similar Vistamaxx Grades Comparison
| Grade | Typical Positioning & Differentiation |
| Vistamaxx 6902 | High flow specialist: MFR 100 g/10min, excellent adhesion, ideal for compounding and modification. |
| Vistamaxx 8580 | Ultra-low viscosity fluidifier for hot melt adhesives and injection molding. |
| Vistamaxx Tough T1600 | High melt strength champion for films and TPO compounding. |
| Vistamaxx 3020FL | Film clarity specialist for blown film and thermoforming. |
Vistamaxx 6902 Typical Properties
| Property | Typical Value | Test Method |
| Density | 0.869 g/cm³ | ASTM D1505 |
| MFR (190°C/2.16kg) | 43 g/10min | ExxonMobil Method |
| MFR (230°C/2.16kg) | 100 g/10min | ExxonMobil Method |
| Ethylene Content | 12 wt% | ExxonMobil Method |
| Hardness | 76 Shore A | ExxonMobil Method |
| Vicat Softening Temperature | 64.1°C | ExxonMobil Method |
| Form | Pellets | Product Data |
Mechanical Property Highlights
| Property | Typical Value |
| Tensile Stress at 100% | 3.4 MPa |
| Tensile Stress at 300% | 3.6 MPa |
| Tensile Strength at Break | > 7.6 MPa |
| Elongation at Break | > 900% |
| Flexural Modulus (1% Secant) | 37 MPa |
| Tear Strength (Die C) | 45.5 kN/m |
Thermal & Processing Guidelines
| Parameter | Typical Recommendation |
| Vicat Softening Temperature | 64.1°C |
| Processing Temperature Window | Wide — starting point ~10°C above highest melting point |
| Drying Requirement | Not required |
| Processing Form | Can be compounded or used as dry blend |
Processing & Performance Notes
- Vistamaxx 6902 can be processed across a wide temperature window without drying.
- A good starting point for processing temperature is about 10°C above the highest melting point of the formulation.
- Conventional processing knowledge should be used to ensure thorough mixing when blending with other polymers.
- Its high flow characteristics make it ideal for compounding applications requiring excellent filler dispersion.
- Typical values are for reference and should not be treated as final product specifications.
Vistamaxx 6902 TDS and Product Documents
| Document | Description | Action |
| TDS | Technical Data Sheet for Vistamaxx 6902, covering physical, mechanical, thermal, and processing properties. | Request TDS |
| SDS | Safety Data Sheet for handling, storage, and safety information. | Request SDS |
| COA | Certificate of Analysis for quality verification and compliance. | Request COA |
Frequently Asked Questions
What is the key feature of Vistamaxx 6902?
Vistamaxx 6902 is characterized by its high melt flow rate (100 g/10min at 230°C) and excellent adhesion to PP and PE, making it ideal for compounding, polymer modification, and hot melt adhesive applications.
Can Vistamaxx 6902 be blended with other polymers?
Yes. Vistamaxx 6902 can be blended with PE, PP, and other polymers including styrenic block copolymers, offering versatility for formulators and compounders.
Is Vistamaxx 6902 RoHS compliant?
Yes. Vistamaxx 6902 is RoHS compliant, making it suitable for environmentally conscious applications and regulatory requirements.
Does Vistamaxx 6902 require drying before processing?
No. This material does not require drying under normal conditions and can be compounded or used as a dry blend with other polyolefins.
What applications is Vistamaxx 6902 suitable for?
This grade is suitable for compounding, polymer modification, hot melt adhesives, and blending applications where high flow, adhesion, and compatibility with polyolefins are required.
Can I request samples and technical documents for Vistamaxx 6902?
Yes. Our team provides full support including samples, TDS, SDS, COA packages, and application-specific guidance to help you evaluate this grade in your compounding or modification application.
Request Vistamaxx 6902 Pricing and Product Documents
Contact us for ExxonMobil Vistamaxx 6902 availability, competitive quotations, sample requests, technical data sheets, safety documentation, and alternative grade matching for your compounding, modification, or adhesive needs.
The information above is based on typical product data and is provided for reference only. Typical values are not specifications. Final material selection should be verified according to processing conditions, application requirements, regulatory needs, and end-use testing. All typical values for Vistamaxx 6902 are industry reference data; actual values may vary by production lot.