Zytel 70G13L NC010 PA66 is a 13% glass fiber reinforced polyamide 66 resin designed for injection molding applications. It provides higher stiffness, improved strength and better dimensional stability than unreinforced PA66 while maintaining good toughness and processability.
This grade is identified as PA66-GF13 and is suitable for demanding engineering components used in automotive, furniture, domestic appliance, sporting goods and construction applications. The NC010 version is the natural color grade, suitable for natural appearance or custom coloring.
Compared with standard PA66 materials, Zytel 70G13L NC010 PA66 offers improved rigidity and dimensional control due to glass fiber reinforcement. Public data lists density around 1.23 g/cm³, tensile modulus around 5500 MPa, tensile stress at break around 120 MPa, and flexural modulus around 4800 MPa.
Shenzhen Ruiqing International Trade Co., Ltd. supplies original Zytel 70G13L NC010 PA66 resin with quotation support, document assistance and global delivery service.
Zytel 70G13L NC010 PA66 Key Features
- 13% glass fiber reinforced PA66
- Natural resin pellet form
- High stiffness and strength
- Good dimensional stability
- Lower shrinkage than unfilled PA66
- Good abrasion and chemical resistance
- Good melt stability
- Suitable for injection molding
Zytel 70G13L NC010 PA66 Typical Applications
- Automotive injection molded parts
- Electrical and electronic components
- Appliance components
- Furniture hardware
- Sporting goods
- Construction components
- Industrial mechanical parts
- Reinforced engineering components
Advantages
Zytel 70G13L NC010 PA66 is suitable for applications requiring better stiffness and dimensional stability than unreinforced nylon 66. Its 13% glass fiber reinforcement gives a balanced level of strength without moving to higher glass-filled grades.
The grade also keeps the main advantages of PA66, including heat resistance, abrasion resistance and chemical resistance, making it useful for durable automotive, electrical and industrial molded parts.
Related Products
Zytel 70G13L NC010 PA66 Typical Properties
| Property | Typical Value |
|---|---|
| Material | PA66-GF13 |
| Grade | 70G13L NC010 |
| Color | Natural |
| Glass Fiber Content | 13% |
| Density | 1.23 g/cm³ |
| Tensile Modulus | 5500 MPa |
| Tensile Stress at Break | 120 MPa |
| Flexural Modulus | 4800 MPa |
| Flexural Stress | 190 MPa |
| Charpy Notched Impact, 23°C | 5 kJ/m² |
| Melting Temperature | 262°C |
| Processing Method | Injection Molding |
Processing Recommendations
Zytel 70G13L NC010 PA66 is recommended for injection molding. Drying before processing is required to control moisture and maintain surface quality, dimensional stability and mechanical performance. Public processing guidance lists drying at 80°C for 2–4 hours, optimum melt temperature around 295°C, and processing moisture content ≤0.2%.
Zytel 70G13L NC010 PA66 FAQ
What is Zytel 70G13L NC010 PA66?
It is a 13% glass fiber reinforced natural PA66 resin designed for injection molding.
What is the main advantage of this grade?
It provides higher stiffness, strength and dimensional stability than unreinforced PA66.
What does PA66-GF13 mean?
PA66-GF13 means polyamide 66 reinforced with approximately 13% glass fiber.
What is the difference between 70G13L and 70G13HS1L?
70G13L is a 13% glass fiber reinforced lubricated PA66 grade, while 70G13HS1L adds heat stabilization for improved thermal aging performance.
Can original Zytel 70G13L NC010 PA66 be supplied?
Yes. Shenzhen Ruiqing International Trade Co., Ltd. can supply original Zytel PA66 materials with quotation and document support.
Request Pricing and Product Documents
Contact Shenzhen Ruiqing International Trade Co., Ltd. for pricing, stock availability and technical support for Zytel 70G13L NC010 PA66 Resin.
Disclaimer
The information above is for reference only. Final material selection and processing conditions should be verified according to official technical documents and actual application requirements.