Micromax 00L1 Low Ohm Chip Resistor Paste
Type: Chip Resistor Paste
Pack: 100G / 1000G
Viscosity: 180 Pa.s
Resistivity: 0.14-0.2 Ω/sq
Firing: 850°C / 30 min
Shelf Life: 6 months
Micromax 00L1 delivers ultra-low resistivity (0.14-0.2 Ω/sq) with exceptional ESD stability and ultra-low noise (≤ -35 dB) — engineered for low resistance chip resistor production with 850°C fast firing.
Micromax 00L1 is a low ohm thick film paste specifically developed for chip resistor applications requiring very low resistance values in the 0.14-0.2 Ω/sq range and ultra-precision electrical performance. This grade delivers exceptional ESD stability with DeltaR of -0.1 to 0.1% using a 100pF/1500Ω network, excellent power handling stability for demanding operating conditions, and ultra-low Quan-Tech noise (≤ -35 dB) for superior signal integrity in sensitive measurement applications. The material offers well controlled TCRs with minimal length and thickness effects across the entire low resistance range.
This resistor paste provides linear blend behavior between adjacent members, enabling broad low resistance coverage without sacrificing electrical properties. It is optimized for high-resolution screen printing at speeds up to 30 cm/sec and supports co-firing with high silver terminations at 850°C peak temperature. The cadmium-free, nickel-free and phthalate-free formulation meets international environmental standards including RoHS and REACH. Standard packaging options are 100G and 1000G.
Genuine Micromax Imported Stock and Technical Support
We maintain stable inventory of authentic Micromax 00L1 low ohm chip resistor paste. Factory-original TDS and batch-specific COA can be provided upon request for electronic component manufacturing projects.
Request Sample, TDS & Quotation
Complete TDS, COA, and regulatory documentation available
Core Advantages of Micromax 00L1
- Ultra-low resistivity range — 0.14-0.2 Ω/sq for very low resistance chip resistor applications
- Exceptional ESD stability — DeltaR of -0.1 to 0.1% for precision electrostatic protection
- Ultra-low Quan-Tech noise — ≤ -35 dB for superior signal integrity in precision circuits
- Excellent power handling stability — reliable performance under varying power loads
- Well controlled TCRs — Hot TCR -100 to 100 ppm/°C, Cold TCR -100 to 100 ppm/°C
- Linear blend behavior — broad low resistance range without sacrificing electrical properties
- Excellent thermal cycle stability — reliable operation under repeated temperature cycling
- RoHS, REACH compliant; Cadmium/Nickel/Phthalate free — satisfies global environmental regulations
Main Applications
- Chip Resistors — ultra-low resistance chip resistor production for precision electronics
- Hybrid Circuits — very low resistance resistor networks for precision measurement
- Surface Mount Devices — low ohm SMD components for industrial and consumer electronics
- Automotive Electronics — low resistance components requiring ESD and thermal cycle stability
- Precision Measurement Equipment — ultra-low noise, very low resistance applications
Full Technical Parameters
| Property | Typical Value | Test / Reference |
| Product Type | Thick film chip resistor paste | — |
| Application | Chip resistor manufacturing | — |
| Packaging Specification | 100G, 1000G | Standard packing |
| Resistivity Range | 0.14-0.2 Ω/sq | Standard geometry |
| Viscosity (Brookfield HAT 10 rpm) | 180 Pa.s | SC4-14/6R, 25°C |
| Recommended Mesh | 250-325 mesh | — |
| Emulsion Thickness | 10-15 μm | — |
| Dried Film Thickness | 18-22 μm | Avoid >22 μm for laser trimmability |
| Leveling Time | 5-10 min | Room temperature |
| Drying Temperature | 150°C | 10-15 minutes |
| Firing Peak Temperature | 850°C | 10 min at peak, 30 min total |
| ESD Stability (DeltaR) | -0.1 to 0.1% | 100pF / 1500Ω network |
| Hot TCR (25-125°C) | -100 to 100 ppm/°C | — |
| Cold TCR (-55-25°C) | -100 to 100 ppm/°C | — |
| Quan-Tech Noise | ≤ -35 dB | Quan-Tech Model 315C |
| Power Handling Stability | Excellent | — |
| Thermal Cycle Stability | Excellent | — |
| Termination Compatibility | High silver terminations (Micromax 5426 Ag/Pd) | — |
| Substrate Compatibility | 96% alumina, Micromax QM44 dielectric | — |
| Blendability | Linear blend behavior between adjacent members | — |
| Environmental Compliance | RoHS, REACH, Cadmium free, Nickel free, Phthalate free | — |
| Shelf Life | 6 months in unopened containers | — |
| Storage Temperature | 5-30°C | — |
Note: All listed values are typical and may vary by batch. Independent qualification testing is required prior to production use.
Recommended Processing Conditions
| Parameter | Recommended Value |
| Screen Mesh | 250-325 mesh |
| Emulsion Thickness | 10-15 μm |
| Dried Film Thickness | 18-22 μm |
| Leveling Time | 5-10 minutes |
| Drying Temperature | 150°C |
| Drying Time | 10-15 minutes |
| Firing Peak Temperature | 850°C |
| Total Firing Cycle | 30 minutes (10 min at peak) |
| Substrate | 96% alumina or Micromax QM44 dielectric |
Handling and Storage Recommendations
| Storage Rules | Store in tightly sealed containers in clean, stable environment at 5-30°C. |
| Shelf Life | 6 months in unopened containers from date of shipment. |
| Pre-use Preparation | Thoroughly mix prior to use. Some settling may occur. |
| Thinning | Not normally required; use Micromax 8250(T) thinner sparingly for evaporative losses. |
Official Technical Documentation
| Document Type | Document Introduction | Document Request |
| TDS | Micromax 00L1 original factory technical data sheet | Request TDS |
| COA | Batch-specific certificate of analysis | Request COA |
| SDS | Safety Data Sheet for handling and storage | Request SDS |
Frequently Asked Questions
What is Micromax 00L1?
Micromax 00L1 is a low ohm thick film paste engineered for chip resistor applications requiring ultra-low resistivity from 0.14-0.2 Ω/sq. It combines exceptional ESD stability with DeltaR of -0.1 to 0.1%, ultra-low noise (≤ -35 dB), excellent power handling, and well controlled TCRs.
What is the resistivity range of Micromax 00L1?
Micromax 00L1 provides an ultra-low resistivity range from 0.14-0.2 Ω/sq, making it suitable for very low resistance chip resistor manufacturing.
What is the viscosity of Micromax 00L1?
Micromax 00L1 exhibits a viscosity of 180 Pa.s when measured with Brookfield HAT at 10 rpm, SC4-14/6R spindle, 25°C.
What is the recommended processing profile for Micromax 00L1?
Recommended processing: level for 5-10 minutes, dry at 150°C for 10-15 minutes, then fire at 850°C peak for 10 minutes within a 30-minute total cycle.
What is the recommended dried film thickness for Micromax 00L1?
Micromax 00L1 is optimized for 18-22 μm dried film thickness using 250-325 mesh screens with 10-15 μm emulsion.
What is the noise performance of Micromax 00L1?
Micromax 00L1 delivers ultra-low Quan-Tech noise of ≤ -35 dB, ensuring superior signal integrity for precision measurement and sensing applications.
Is Micromax 00L1 environmentally compliant?
Yes. Micromax 00L1 contains no intentionally added cadmium, nickel or phthalates, meeting RoHS and REACH environmental compliance requirements.
What terminations are compatible with Micromax 00L1?
Micromax 00L1 is compatible with high silver terminations, with reported properties obtained using Micromax 5426 Ag/Pd termination.
What packaging sizes are available for Micromax 00L1?
Micromax 00L1 is supplied in 100G and 1000G containers. For larger volume requirements, please contact our sales team.
Get Micromax 00L1 Bulk Pricing and Technical Support
We supply genuine Micromax 00L1 low ohm chip resistor paste for electronic component manufacturing. Contact us for bulk pricing, sample availability, technical documents, and application support.
Inquire Bulk Price & Technical Support
Disclaimer: All technical data on this page are for general guidance only and are not product specifications. Buyers must carry out independent trials and verify suitability before bulk ordering. Actual values may vary between production lots.