MacDermid Alpha Micromax 5093D PTC Thermistor Composition for Temperature Sensors
Type: PTC Thermistor Composition
Application: Temperature Sensors
Series: 5091D / 5092D / 5093D
Shelf Life: 6 months
Micromax 5093D is a positive temperature coefficient thermistor composition for thick film microcircuits. It provides linear resistance versus temperature response and high positive TCR, with post laser trim stability below 0.2% at 25°C, 85%RH/85°C, and 150°C over 1000 hours. Blendable with 5091D and 5092D.
Micromax 5093D from MacDermid Alpha is a positive temperature coefficient (PTC) thermistor composition designed for making PTC thermistors in thick film microcircuits using conventional thick film processing. It is the third member of the blendable 5091D / 5092D / 5093D series, which allows resistance and TCR tuning without changing process conditions. Target applications include temperature sensors, temperature compensation elements, and heaters. Post laser trim stability is below 0.2% across all three test conditions.
The paste has a viscosity range of 150–250 Pa.s and uses Micromax 4553 as the recommended thinner. Terminations are typically Micromax 7484 Ag/Pd prefired at 850°C; Ag Micromax 6160 has also been tested. Print with a 200-mesh stainless steel screen with 15±3 μm emulsion to a dried print thickness of 25±2 μm. Allow prints to level 5–10 minutes, then dry 10–15 minutes at 150°C. Fire on a 30-minute profile with a 10-minute peak at 850°C. Post laser trim stability is <0.2% at 25°C/1000 hrs, <0.2% at 85%RH/85°C/1000 hrs, and <0.2% at 150°C/1000 hrs. Glass encapsulation is not generally required, but Micromax 9137 or QQ550 fired at 500°C is recommended when mechanical or environmental protection is needed. Store sealed at 5–30°C; unopened shelf life is 6 months.
Genuine MacDermid Alpha Micromax Imported Stock & Technical Support
We hold regular stock of authentic MacDermid Alpha Micromax 5093D PTC thermistor composition. Original factory TDS and batch-specific COA are available on request for your thick film microcircuit programs.
Request Sample, TDS & Quotation
Complete TDS, COA, and regulatory documentation available
Key Features of MacDermid Alpha Micromax 5093D
- PTC thermistor composition for thick film microcircuits
- Linear resistance dependence on temperature
- High positive TCR for sensitive thermal response
- Blendable with 5091D and 5092D to tune target resistance
- Post laser trim stability below 0.2% at 25°C, 85%RH/85°C, and 150°C over 1000 hours
- Compatible with conventional thick film processing
- Suited to temperature sensors, compensation elements, and heaters
- Viscosity 150–250 Pa.s for screen printing
- Screen build: 200-mesh stainless steel, 15±3 μm emulsion
- Dried print thickness 25±2 μm
- Firing: 30-minute profile, 10-minute peak at 850°C
- Glass encapsulation not generally required; Micromax 9137 or QQ550 available if needed
Primary Applications
- Temperature sensors — PTC elements for thermal sensing circuits
- Temperature compensation — resistance tracking with temperature
- Heaters — self-regulating PTC heating elements
- Thick film microcircuits — chip resistor and microcircuit builds
Full Technical Specifications
| Property | Typical Value | TDS Reference |
| Product Type | PTC thermistor composition | TDS: PTC Thermistor Composition |
| Application | Chip resistor | TDS: Chip resistor |
| Solvent or Thinner | Micromax 4553 | TDS: Micromax 4553 |
| Blend Member or Series | 5091D / 5092D / 5093D | TDS: 5091D/5092D/5093D |
| Viscosity | 150 to 250 Pa.s | TDS: Brookfield HAT, 10 rpm, 25°C |
| Terminations | Micromax 7484 Ag/Pd prefired at 850°C; Ag Micromax 6160 also tested | TDS: Terminations |
| Substrate Compatibility | 96% alumina | TDS: 96% alumina |
| Screen Mesh | 200 mesh stainless steel with 15±3 μm emulsion | TDS: 200-mesh, 15±3μm |
| Dried Print Thickness | 25 ± 2 μm | TDS: 25±2μm |
| Leveling | 5 to 10 minutes at room temperature | TDS: 5-10 minutes |
| Drying Schedule | 10 to 15 minutes at 150°C | TDS: 10-15 minutes at 150°C |
| Firing Profile | 30-minute profile with 10-minute peak at 850°C | TDS: 850°C, 10 min peak, 30 min profile |
| Post Laser Trim Stability (25°C/1000 hrs) | < 0.2 % | TDS: < 0.2 |
| Post Laser Trim Stability (85%RH/85°C/1000 hrs) | < 0.2 % | TDS: < 0.2 |
| Post Laser Trim Stability (150°C/1000 hrs) | < 0.2 % | TDS: < 0.2 |
| Encapsulant | Not generally required; Micromax 9137 or QQ550 fired at 500°C if protection needed | TDS: Encapsulant |
| Shelf Life | 6 months | TDS: 6 months |
| Storage Temperature | 5 - 30 °C | TDS: 5°C - 30°C |
Note: All listed values are typical and may vary by batch. Values based on MacDermid Alpha official TDS. Independent qualification testing is required prior to production use.
Recommended Processing Conditions
| Parameter | Recommended Value | TDS Reference |
| Mixing Prior to Use | Thoroughly mix to redisperse solids | TDS: thoroughly mix |
| Screen Mesh | 200 mesh stainless steel with 15±3 μm emulsion | TDS: 200-mesh, 15±3μm |
| Dried Print Thickness | 25 ± 2 μm | TDS: 25±2μm |
| Leveling | 5–10 minutes at room temperature | TDS: 5-10 minutes |
| Drying | 10–15 minutes at 150°C | TDS: 10-15 minutes at 150°C |
| Firing | 30-minute profile with 10-minute peak at 850°C | TDS: 850°C, 10 min peak |
| Encapsulation (optional) | Micromax 9137 or QQ550 fired at 500°C, when protection is needed | TDS: Encapsulant |
| Thinner | Micromax 4553 | TDS: Micromax 4553 |
Handling and Storage Recommendations
| Storage Rules | Store tightly sealed in a clean, stable environment at 5-30°C. | TDS: 5°C - 30°C |
| Shelf Life | 6 months in unopened containers from date of shipment. | TDS: 6 months |
| Pre-use Preparation | Thoroughly mix prior to use. Some settling of solids may occur during storage. | TDS: thoroughly mix |
| Transportation | Under normal shipping conditions, no temperature control is expected. For extended transport periods, confirm product suitability. | TDS: normal shipping conditions |
Official Technical Documentation
| Document Type | Document Introduction | Document Request |
| TDS | MacDermid Alpha Micromax 5093D original factory technical data sheet | Request TDS |
| COA | Batch-specific certificate of analysis | Request COA |
| SDS | Safety Data Sheet for handling and storage | Request SDS |
Frequently Asked Questions
How does 5093D fit within the PTC series?
5093D is part of the blendable 5091D / 5092D / 5093D series. It shares the same process conditions as the other two grades and delivers the same tight post laser trim stability, under 0.2% across all three test conditions.
What makes 5093D suitable for temperature sensors?
The TDS lists linear dependence of resistance with temperature and high positive TCR as key benefits. That combination lets the resistor track temperature predictably, which fits sensing and compensation circuits.
Which terminations work with 5093D?
Reported properties are based on Micromax 7484 Ag/Pd conductor prefired at 850°C. Excellent results have also been obtained with Ag Micromax 6160, prefired at 850°C.
How stable is 5093D after laser trimming?
Post laser trim stability is below 0.2% at 25°C over 1000 hours, below 0.2% at 85%RH/85°C over 1000 hours, and below 0.2% at 150°C over 1000 hours. The test used 1.5×1.5mm resistors trimmed to 1.5× initial value with a single plunge cut.
Is encapsulation needed for 5093D?
In general, no. The TDS notes glass encapsulation is not required for standard use. For mechanical protection or extreme environments such as high temperature nitrogen or forming gas, Micromax 9137 or QQ550 fired at 500°C is recommended.
Can firing profile changes affect 5093D performance?
Yes. The TDS notes that longer firing profiles or higher peak temperatures will cause slight variation in resistance and TCR. Keeping the recommended 30-minute profile with a 10-minute peak at 850°C helps maintain the rated values.
What thinner should be used with 5093D?
Micromax 4553 is the listed solvent or thinner. Using the recommended thinner helps keep viscosity and print behavior consistent with the TDS values.
Get MacDermid Alpha Micromax 5093D Bulk Pricing and Technical Support
We supply authentic MacDermid Alpha Micromax 5093D PTC thermistor composition for thick film microcircuit programs. Contact our team for bulk quotations, sample availability, technical documentation, and application support.
Inquire Bulk Price & Technical Support
Disclaimer: All technical data on this page are for general guidance only and are not product specifications. Buyers must carry out independent trials and verify suitability before bulk ordering. Actual values may vary between production lots.